Mechanical properties	Test Condition	Test Method	APPC SAUDI/1101R
elongation at break	50mm/min	ISO 527-2	>50 %
tensile strength	50mm/min	ISO 527-2	34 Mpa
elongation at yield	50mm/min	ISO 527-2	8 %
Tensile modulus	1mm/min	ISO 527-2	1500 Mpa
Impact strength of simply supported beam without notch	23℃	ISO 179/1eU	110 kJ/m²
Charpy Notched Impact Strength	23℃	ISO 179/1eU	2.5 kJ/m²
ball-indentation hardness	H358/30	ISO 2039-1	78 Mpa

physical property	Test Condition	Test Method	APPC SAUDI/1101R
melt mass-flow rate	230℃，2.16kg	ISO 1133	24 g/10min
density		ISO 1183	0.91 g/cm³

Thermal performance	Test Condition	Test Method	APPC SAUDI/1101R
Heat distortion temperature	0.45MPa，HDT	ISO 75-2	85 °C
vicat	A50(10N)	ISO 306	154 °C
melting temperature		ISO 3146	163 °C