PA6 73G15HSL BK363 DUPONT USA
Zytel®
Automotive components、Industrial machinery
Thermal stability、High crystallinity
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
physical property
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
Shrinkage rate
TD
ISO294-4
%
0
Shrinkage rate
MD
ISO294-4
%
0
Water absorption rate
饱和,23°C,2.00mm
ISO62
%
7
Water absorption rate
平衡,23°C,2.00mm,50%RH
ISO62
%
2
Mechanical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
elongation at break
ASTM D638/ISO 527
%
2
Impact strength of simply supported beam without notch
-30°C
ISO179/1eU
kJ/m²
4
Impact strength of simply supported beam without notch
23°C
ISO179/1eU
kJ/m²
4
Tensile modulus
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
6
Tensile modulus
ISO527-2
Mpa
6
tensile strength
断裂
ISO527-2
Mpa
1
tensile strength
ASTM D638/ISO 527
kg/cm²(MPa)[Lb/in²]
1
elongation
断裂
ISO527-2
%
2
Impact strength of cantilever beam gap
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
4
Charpy impact strength
ASTM D256/ISO 179
kg·cm/cm(J/M)ft·lb/in
6
Thermal performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
Hot deformation temperature
0.45MPa,未退火
ISO75-2/B
°C
2
Hot deformation temperature
1.8MPa,未退火
ISO75-2/A
°C
2
Hot deformation temperature
ASTM D648/ISO 75
℃（℉）
2
Melting temperature
ISO11357-3
°C
2
vicat softening point
ISO306/B50
°C
2
Linear coefficient of thermal expansion
MD：--
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
MD：-40to23°C
ISO11359-2
cm/cm/°C
3
Linear coefficient of thermal expansion
MD：55to160°C
ISO11359-2
cm/cm/°C
1
Linear coefficient of thermal expansion
TD：--
ISO11359-2
cm/cm/°C
9
Linear coefficient of thermal expansion
TD：-40to23°C
ISO11359-2
cm/cm/°C
7
Linear coefficient of thermal expansion
TD：55to160°C
ISO11359-2
cm/cm/°C
1
Electrical performance
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
Dielectric strength
IEC60243-1
KV/mm
2
flammability
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
Fogging-G-value
condensate
ISO6452
g
0
Extreme Oxygen Index
ISO4589-2
%
2
Burning rate
1.00mm
ISO3795
mm/min
2
Supplementary Information
Test Condition
Test Method
Unit
PA6/DUPONT USA/73G15HSL BK363
EmissionofOrganicCompounds
VDA277
µgC/g
8