PA6 Comco PA 6 G heat stabilized Comco Nylon GmbH
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Charpy Notched Impact Strength | kJ/m² | 3.5 -- | |
| Impact strength of cantilever beam gap | kJ/m² | 3.5 6.0 | |
| Impact strength of simply supported beam without notch | 无断裂 -- |
| hardness | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Rockwell hardness | M计秤 | 85 -- | |
| ball-indentation hardness | MPa | 160 -- | |
| Shore hardness | 邵氏D | 80 -- |
| Mechanical properties | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Tensile creep modulus | 1000hr | MPa | 21.0 10.0 |
| compression stress | 5%应变 | MPa | 85.0 -- |
| 2%应变 | MPa | 48.0 -- | |
| 1%应变 | MPa | 25.0 -- | |
| Tensile strain | 断裂,23°C | % | 15 >50 |
| tensile strength | 屈服,23°C | MPa | 80.0 50.0 |
| Tensile modulus | 23°C | MPa | 3200 1500 |
| Electrical performance | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Surface Resistivity | ohms | >1.0E+13 >1.0E+12 | |
| relative permittivity | 1MHz | 3.20 3.70 | |
| dielectric strength | kV/mm | 25 17 | |
| Volume resistivity | ohms·cm | >1.0E+14 >1.0E+12 | |
| Dissipation Factor | 100Hz | 0.012 0.14 | |
| relative permittivity | 100Hz | 3.60 6.60 | |
| Compared to the Leakage Tracking Index (CTI) | V | PLC 0 | |
| Dissipation Factor | 1MHz | 0.016 0.050 |
| flammability | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Limiting Oxygen Index | % | 25 -- | |
| UL flame retardant rating | 3.00mm | HB -- | |
| 6.00mm | HB -- |
| physical property | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| density | g/cm³ | 1.15 -- | |
| Water absorption rate | 饱和,23°C | % | 6.6 -- |
| after24himmersioninwater:23°C | mg | 50.0 -- | |
| after96himmersioninwater:23°C | mg | 94.0 -- | |
| 平衡,23°C,50%RH | % | 2.4 -- |
| Thermal performance | Test Condition | Test Method | Comco Nylon GmbH/Comco PA 6 G heat stabilized |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD：23到100°C | cm/cm/°C | 9E-05 -- |
| melting temperature | °C | 220 -- | |
| Linear coefficient of thermal expansion | MD：23到60°C | cm/cm/°C | 8E-05 -- |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 80.0 -- |
| thermal conductivity | W/m/K | 0.29 -- | |
| Minimum operating temperature | °C | -40 -- | |
| maximum service temperature | inaircontinuosly | °C | 120 -- |
| inairforshortperiods | °C | 170 -- |