Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 420SE0-7001 SABIC INNOVATIVE THAILAND
VALOX™
Lawn equipment、Garden equipment、Industrial applications、Automotive External Parts、Electrical field、Electronic field、Architectural application、Outdoor applications、Electrical appliances、Engine hood parts、Medical supplies、Nursing supplies、Plastic bag、Automotive interior parts、Casters、Household goods、Petroleum Applications、Natural gas supplies、sporting goods、Textile application、Lighting applications
Glass fiber reinforced、dimensional stability 、High rigidity、high strength、heat-resisting
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Dart impact equipped with measuring instruments | 23°C, Total Energy | ASTM D3763 | 5.00 J |
| Unnotched Izod Impact Strength | -30°C 8 | ISO 180/1U | 45 kJ/m² |
| The impact strength of a simply supported beam without a notch is 7 | -30°C | ISO 179/1eU | 50 kJ/m² |
| Impact strength of simply supported beam gap 7 | -30°C | ISO 179/1eA | 6.0 kJ/m² |
| 23°C | ISO 179/1eA | 7.0 kJ/m² | |
| The impact strength of a simply supported beam without a notch is 7 | 23°C | ISO 179/1eU | 50 kJ/m² |
| Unnotched Izod Impact Strength | 23°C 8 | ISO 180/1U | 45 kJ/m² |
| 23°C | ASTM D4812 | 620 J/m |
| hardness | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Ball Indentation Hardness | H 358/30 | ISO 2039-1 | 118 Mpa |
| Rockwell hardness | R 计秤 | ISO 2039-2 | 119 |
| R 级 | ASTM D785 | 119 |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Flexural modulus | -- 6 | ISO 178 | 9500 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 120 Mpa |
| elongation | 屈服 4 | ASTM D638 | 2.0 % |
| 屈服 | ISO 527-2/5 | 1.9 % | |
| Bending stress | 断裂, 50.0 mm 跨距 5 | ASTM D790 | 186 Mpa |
| Tensile modulus | -- 3 | ASTM D638 | 12000 Mpa |
| tensile strength | 屈服 4 | ASTM D638 | 120 Mpa |
| Bending stress | -- | ISO 178 | 180 Mpa |
| Flexural modulus | 50.0 mm 跨距 5 | ASTM D790 | 9800 Mpa |
| tensile strength | 断裂 4 | ASTM D638 | 120 Mpa |
| 屈服 | ISO 527-2/5 | 120 Mpa | |
| Taber Abrasion Resistance | 1000 Cycles, 1000 g, CS-17 转轮 | 内部方法 | 22.0 mg |
| Tensile modulus | -- | ISO 527-2/1 | 10000 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 1.9 % |
| 断裂 4 | ASTM D638 | 2.0 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 24 KV/mm |
| 0.800 mm, 在油中 | IEC 60243-1 | 23 KV/mm | |
| dielectric constant | 50 Hz | IEC 60250 | 3.30 |
| CTI | -- | IEC 60112 | 175 V |
| dielectric constant | 100 Hz | ASTM D150, IEC 60250 | 3.80 |
| 1 MHz | ASTM D150 | 3.70 | |
| Dissipation Factor | 50 Hz | IEC 60250 | 1.0E-3 |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 3 | |
| High arc combustion index (HAI) | UL 746 | PLC 0 | |
| dielectric strength | 1.60 mm, 在油中 | IEC 60243-1 | 22 KV/mm |
| dielectric constant | 60 Hz | IEC 60250 | 3.30 |
| Dissipation Factor | 1 MHz | IEC 60250 | 0.010 |
| Volume resistivity | ASTM D257, IEC 60093 | > 1.0E+15 ohms·cm | |
| CTI | 解决方案 B | IEC 60112 | 125 V |
| Dissipation Factor | 100 Hz | ASTM D150, IEC 60250 | 2.0E-3 |
| 60 Hz | IEC 60250 | 1.0E-3 | |
| Hot wire ignition (HWI) | UL 746 | PLC 2 | |
| dielectric strength | 3.20 mm, in Air | ASTM D149 | 19 KV/mm |
| Arc resistance 11 | ASTM D495 | PLC 6 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 4 | |
| Surface Resistivity | IEC 60093 | > 1.0E+15 ohms | |
| dielectric strength | 3.20 mm, 在油中 | IEC 60243-1 | 16 KV/mm |
| Dissipation Factor | 1 MHz | ASTM D150 | 0.020 |
| dielectric constant | 1 MHz | IEC 60250 | 3.30 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| UL flame retardant rating | 0.71 mm | UL 94 | V-0 |
| 0.40 mm | UL 94 | V-2 | |
| 2.0 mm | UL 94 | 5VA | |
| Burning wire flammability index | 1.0 mm | IEC 60695-2-12 | 960 °C |
| Limiting Oxygen Index | ISO 4589-2 | 32 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Shrinkage rate | 横向流动 2 | 内部方法 | 0.40 到 0.80 % |
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.070 % |
| Shrinkage rate | 横向流动 : 3.20 mm | 内部方法 | 0.50 到 1.0 % |
| 流动 2 | 内部方法 | 0.10 到 0.50 % | |
| Outdoor applicability | UL 746C | f2 | |
| Molten Volume Flow Rate (MVR) | 250°C/5.0 kg | ISO 1133 | 29.0 cm3/10min |
| melt mass-flow rate | 250°C/5.0 kg | ASTM D1238 | 42 g/10 min |
| Specific volume | ASTM D792 | 0.610 cm³/g | |
| Shrinkage rate | 流动 : 3.20 mm | 内部方法 | 0.50 到 0.70 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 0.090 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Linear thermal expansion coefficient | 流动 : 23 到 80°C | ISO 11359-2 | 2.5E-5 cm/cm/°C |
| 流动 : -40 到 40°C | ASTM E831, ISO 11359-2 | 2.5E-5 cm/cm/°C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 3.20 mm | ASTM D648 | 212 °C |
| Linear thermal expansion coefficient | 横向 : -40°C | ISO 11359-2 | 8.9E-5 cm/cm/°C |
| RTI | UL 746 | 140 °C | |
| Thermal deformation temperature under load | 0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Be | 220 °C |
| Linear thermal expansion coefficient | 横向 : 23 到 80°C | ISO 11359-2 | 1.2E-4 cm/cm/°C |
| thermal conductivity | ISO 8302 | 0.25 W/m/K | |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距 9 | ISO 75-2/Ae | 195 °C |
| Linear thermal expansion coefficient | 横向 : -40 到 40°C | ASTM E831 | 8.9E-5 cm/cm/°C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 3.20 mm | ASTM D648 | 200 °C |
| vicat | -- | ISO 306/A50 | 220 °C |
| Ball Pressure Test | 123 到 127°C | IEC 60695-10-2 | 通过 |
| vicat | -- | ASTM D152510, ISO 306/B50, ISO 306/B120 | 200 °C |
| Thermal deformation temperature under load | 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距 8 | ISO 75-2/Af | 200 °C |
| RTI Imp | UL 746 | 130 °C | |
| RTI Elec | UL 746 | 130 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE THAILAND/420SE0-7001 |
|---|---|---|---|
| Nozzle Temperature | 250 到 270 °C | ||
| Processing (melt) temperature | 255 到 275 °C | ||
| drying temperature | 120 °C | ||
| Exhaust hole depth | 0.025 到 0.038 mm | ||
| Temperature at the front of the material cylinder | 255 到 275 °C | ||
| Suggested maximum moisture content | 0.020 % | ||
| Temperature in the middle of the barrel | 250 到 270 °C | ||
| Temperature | 65 到 90 °C | ||
| screw speed | 50 到 80 rpm | ||
| Temperature at the rear of the barrel | 245 到 265 °C | ||
| Back pressure | 0.300 到 0.700 Mpa | ||
| drying time | 3.0 到 4.0 hr | ||
| Suggested injection volume | 40 到 80 % |