PA66 HTN51G35FWS BK083 DUPONT USA
Zytel®
Automotive interior parts,Fitness equipment,electrical equipment
Glass fiber reinforced,Thermal stability,High temperature resistan,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| -30°C | ISO 179/1eU | 60 kJ/m² |
| hardness | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 124 |
| M计秤 | ISO 2039-2 | 108 |
| Supplementary Information | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| Odor | VDA270 | 4.00 |
| thermal performance | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| 0.45MPa,未退火，HDT | ISO 75-2/B | 284 °C | |
| Linear coefficient of thermal expansion | TD：-40to23°C | ISO 11359-2 | 5.5E-05 cm/cm/°C |
| MD：-- | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| MD：-40to23°C | ISO 11359-2 | 1.8E-05 cm/cm/°C | |
| TD：-- | ISO 11359-2 | 5.5E-05 cm/cm/°C | |
| melting temperature | ISO 11357-3 | 300 °C |
| mechanical properties | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| Poisson's ratio | ISO 527 | 0.39 | |
| Tensile creep modulus | 1hr | ISO 899-1 | -- Mpa |
| Tensile modulus | ISO 527-2 | 12000 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 210 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | 2.4 % |
| bending strength | ISO 178 | 300 Mpa | |
| Tensile creep modulus | 1000hr | ISO 899-1 | -- Mpa |
| flexural modulus | ISO 178 | 10300 Mpa |
| Electrical performance | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 36 KV/mm | |
| relative permittivity | 100Hz | IEC 60250 | 4.00 |
| volume resistivity | IEC 60093 | >1.0E+15 ohms·cm | |
| relative permittivity | 1MHz | IEC 60250 | 4.00 |
| Surface Resistivity | IEC 60093 | -- ohms | |
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | V |
| Physical properties | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| ThermalConductivityofMelt | 0.25 W/m/K | ||
| SpecificHeatCapacity of Melt | 1860 J/kg/°C | ||
| shrinkage rate | TD | ISO 294-4 | 0.60 % |
| Water absorption rate | 饱和,23°C,2.00mm | ISO 62 | 4.5 % |
| shrinkage rate | MD | ISO 294-4 | 0.20 % |
| flammability | Test Condition | Test Method | DUPONT USA/HTN51G35FWS BK083 |
|---|---|---|---|
| UL flame retardant rating | 0.9mm | IEC 60695-11-10,-20 | HB |
| 1.5mm | IEC 60695-11-10,-20 | HB | |
| FMVSS flammability | FMVSS302 | B | |
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| Limiting Oxygen Index | ISO 4589-2 | 24 % | |
| UL flame retardant rating | 0.9mm | UL 94 | HB |
| burning rate | 1.00mm | ISO 3795 | 23 mm/min |