Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PP M2 N01 LYONDELLBASELL HOLAND
Moplen
component、Engine hood parts
High rigidity、Homopolymer、Low flow、Mineral filler、20% filler by weight、Good rigidity、Homopolymer、Low liquidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | LYONDELLBASELL HOLAND/M2 N01 |
|---|---|---|---|
| tensile strength | 屈服 | ISO 527-2/50 | 32.0 Mpa |
| Tensile modulus | 正割 | ISO 527-2 | 2700 Mpa |
| ball-indentation hardness | H 358/30 | ISO 2039-1 | 85.0 Mpa |
| Flexural modulus | 正割 | ISO 178 | 2850 Mpa |
| Charpy Notched Impact Strength | -20℃ | ISO 179/1eA | 2.0 kJ/m² |
| Impact strength of simply supported beam without notch | -20℃ | ISO 179/1eU | 20 kJ/m² |
| physical property | Test Condition | Test Method | LYONDELLBASELL HOLAND/M2 N01 |
|---|---|---|---|
| melt mass-flow rate | 230℃/5.0 kg | ISO 1133 | 9.0 g/10 min |
| Melt volume flow rate | 230℃/5.0 kg | ISO 1133 | 10.0 cm3/10min |
| Thermal performance | Test Condition | Test Method | LYONDELLBASELL HOLAND/M2 N01 |
|---|---|---|---|
| Heat distortion temperature | 0.45 MPa, 未退火，HDT | ISO 75-2/B | 120 °C |
| 1.8 MPa, 未退火，HDT | ISO 75-2/A | 70.0 °C |