PPO(PPE) VESTORAN® 1900 Altuglas International of Arkema Inc.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C,完全断裂 | ISO 179/1eA | 25 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C,局部断裂 | ISO 179/1eU | 250 kJ/m² |
| Supplementary Information | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| ElectrolyticalCorrosion-Step | IEC 60426 | A1 |
| Mechanical properties | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 2000 MPa | |
| Tensile strain | 断裂 | ISO 527-2 | 50 % |
| 屈服 | ISO 527-2 | 6.0 % | |
| tensile strength | 屈服 | ISO 527-2 | 60.0 MPa |
| Flexural modulus | ISO 178 | 2400 MPa |
| Electrical performance | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 40 kV/mm | |
| Volume resistivity | IEC 60093 | 1E+13 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 8E-04 |
| relative permittivity | 100Hz | IEC 60250 | 2.60 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A5 | IEC 60112 | PLC 3 |
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Compared to the Leakage Tracking Index (CTI) | 解决方案A | IEC 60112 | PLC 3 |
| Surface Resistivity | IEC 60093 | 1E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 1.6E-03 |
| flammability | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| UL flame retardant rating | 0.8mm | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| Shrinkage rate | TD:80°C,2.00mm | ISO 294-4 | 0.80 % |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.40 % |
| density | ISO 1183 | 1.04 g/cm³ | |
| Shrinkage rate | MD:80°C,2.00mm | ISO 294-4 | 0.90 % |
| Melt volume flow rate | 300°C/21.6kg | ISO 1133 | 40.0 cm³/10min |
| Thermal performance | Test Condition | Test Method | Altuglas International of Arkema Inc./VESTORAN® 1900 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 190 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 170 °C | |
| vicat | -- | ISO 306/B | 185 °C |
| -- | ISO 306/A | 190 °C |