PPO(PPE)+PS Generic PPE+PS+Nylon - Mineral Generic
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Generic/Generic PPE+PS+Nylon - Mineral |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 3.5to4.0 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 4.0to4.5 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Generic/Generic PPE+PS+Nylon - Mineral |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 4000to4440 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0to7.0 % |
| Tensile modulus | 23°C | ISO 527-2 | 4200to4790 MPa |
| tensile strength | 断裂,23°C | ISO 527-2 | 60.0to65.0 MPa |
| bending strength | 23°C | ISO 178 | 105to110 MPa |
| physical property | Test Condition | Test Method | Generic/Generic PPE+PS+Nylon - Mineral |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.20to1.25 g/cm³ |
| Shrinkage rate | MD：23°C | ASTM D955 | 0.80to1.1 % |
| Thermal performance | Test Condition | Test Method | Generic/Generic PPE+PS+Nylon - Mineral |
|---|---|---|---|
| vicat | ISO 306 | 185to200 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 184to205 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 5.0E-5到6.0E-5 cm/cm/°C |
| TD | ISO 11359-2 | 6.5E-05 cm/cm/°C |