PBT B 4406 G3 BASF GERMANY
Ultradur®
Thin walled components、Switch panel、Shell、Electrical components、Laptop case
Glass fiber reinforced、Flame retardant、High mobility
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179 | 6.5 kJ/m² |
| -30°C | ISO 179 | 6.5 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180 | 6.1 kJ/m² |
| -30°C | ISO 180 | 6.1 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 32 kJ/m² |
| Mechanical properties | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 2.7 % |
| Flexural modulus | 23°C | ISO 178 | 6050 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 6500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 110 Mpa |
| Electrical performance | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| Volume resistivity | IEC 60093 | >1.0E+13 ohms·cm |
| flammability | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |
| 3.0mm | UL 94 | V-0 | |
| 1.5mm | UL 94 | V-0 | |
| 0.40mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| density | ISO 1183 | 1.55 g/cm³ | |
| Melt volume flow rate | 250°C/2.16kg | ISO 1133 | 13.0 cm3/10min |
| Viscosity value | 降低的粘度 | ISO 1628 | 116.0 ml/g |
| Thermal performance | Test Condition | Test Method | BASF GERMANY/B 4406 G3 |
|---|---|---|---|
| RTI Str | 0.75mm | UL 746 | 125 °C |
| RTI Imp | 1.5mm | UL 746 | 130 °C |
| RTI Elec | 3.0mm | UL 746 | 140 °C |
| 0.40mm | UL 746 | 75.0 °C | |
| RTI Imp | 3.0mm | UL 746 | 130 °C |
| melting temperature | ISO 3146 | 223 °C | |
| RTI Elec | 0.75mm | UL 746 | 140 °C |
| RTI Imp | 0.40mm | UL 746 | 75.0 °C |
| 0.75mm | UL 746 | 130 °C | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 217 °C |
| RTI Str | 1.5mm | UL 746 | 130 °C |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 195 °C |
| RTI Str | 3.0mm | UL 746 | 130 °C |
| RTI Elec | 1.5mm | UL 746 | 140 °C |
| RTI Str | 0.40mm | UL 746 | 75.0 °C |