PC/ABS CY5100-701 SABIC INNOVATIVE NANSHA
CYCOLOY™
Shell,Electronic and electrical components
Ultra high melting finger,Aging resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| Surface Resistivity | ASTM D257/IEC 60093 | 1.0E+15 ohm.cm Ω | |
| dielectric constant | ASTM D150/IEC 60250 | 2.90 | |
| arc resistance | ASTM D495/IEC 60112 | -- | |
| Volume resistivity | ASTM D257/IEC 60093 | 1.0E+15 ohms Ω.cm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 13700 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 354000 kg/cm²(MPa)[Lb/in²] | |
| elongation | ASTM D638/ISO 527 | 4.1/4.0 % | |
| Tensile modulus | ASTM D638/ISO 527 | 400000(399000) kg/cm²(MPa)[Lb/in²] | |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | -- kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 65/35 % | |
| Rockwell hardness | ASTM D785 | -- | |
| tensile strength | ASTM D638/ISO 527 | 9270(6890)/9150(6730) kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| characteristic | 加阻燃V-1-V-0.无卤.无溴.高流动.高抗冲 | ||
| notes | 注射成型 | ||
| Color | 本色 | ||
| purpose | -- |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.40-0.60 % | |
| density | ASTM D792/ISO 1183 | 1.18 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 260℃/2.16kg.1.40 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 0.60 % |
| processability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| process temperature | 464-554 °C | ||
| pressure | -- Mpa | ||
| Dry conditions | 干燥温度：176-194℉.干燥时间:2.0-4.0hr | ||
| screw speed | -- rpm | ||
| Melt Temperature | 482-572 °C | ||
| Temperature | 140-185 °C |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/CY5100-701 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-1-V-0 | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 191 ℃（℉） |
| vicat | ASTM D1525/ISO R306 | 220-223 ℃（℉） | |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 0.000044 mm/mm.℃ |