Material Comparison

Product Info
Product Name
Brand Name
Usages
Properties
Certificates
MABS XG568 LG CHEM KOREA
--
TV casing、Electronic field、Electrical field
Scratch resistant、High gloss
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

hardnessTest ConditionTest MethodLG CHEM KOREA/XG568
Rockwell hardnessR 级, 23°C, 注塑ASTM D785115
Mechanical propertiesTest ConditionTest MethodLG CHEM KOREA/XG568
bending strength23°C, 3.20 mm, 注塑ASTM D79090.0 Mpa
Tensile modulus23°C, 3.20 mm, 注塑ASTM D6382650 Mpa
Flexural modulus23°C, 3.20 mm, 注塑ASTM D7902850 Mpa
tensile strength 屈服, 23°C, 3.20 mm, 注塑ASTM D63855.0 Mpa
elongation断裂, 23°C, 3.20 mm, 注塑ASTM D638> 15 %
flammabilityTest ConditionTest MethodLG CHEM KOREA/XG568
UL flame retardant rating3.2 mmUL 94HB
1.5 mmUL 94HB
physical property Test ConditionTest MethodLG CHEM KOREA/XG568
melt mass-flow rate220°C/10.0 kgASTM D123818 g/10 min
Shrinkage rate23°C, 3.20 mm, 注塑，FlowASTM D9550.40 - 0.70 %
Thermal performanceTest ConditionTest MethodLG CHEM KOREA/XG568
Heat distortion temperature1.8 MPa, 未退火, 6.40 mm, 注塑，HDTASTM D64882.0 °C
RTI ImpUL 74650.0 °C
RTIUL 74650.0 °C
vicatASTM D1525790.0 °C
RTI ElecUL 74650.0 °C
injectionTest ConditionTest MethodLG CHEM KOREA/XG568
drying time3.0 to 4.0 hr
screw speed30 to 60 rpm
Temperature in the middle of the barrel190 to 210 °C
Temperature at the rear of the barrel180 to 200 °C
Processing (melt) temperature200 to 230 °C
drying temperature80 to 90 °C
Temperature at the front of the material cylinder200 to 220 °C
Back pressure0.981 to 2.94 Mpa
Temperature40 to 60 °C
Spray nozzle temperature200 to 230 °C