Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates

PC HFD1910-NA9E108T SABIC INNOVATIVE NANSHA
LEXAN™
Electrical applications,Automotive Applications,Mechanical accessories
High mobility,Hydrolysis resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 60 kJ/m² |
Dart impact | 23°C,TotalEnergy | ASTM D3763 | 56.0 J |
Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | NoBreak |
Multi axis Instrumented Impact Energy | ISO 6603-2 | 92.0 J | |
Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 11 kJ/m² |
Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | NoBreak |
Impact strength of cantilever beam gap | -30°C | ISO 180/1A | 10 kJ/m² |
Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | NoBreak |
Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 55 kJ/m² |
Suspended wall beam without notch impact strength | -30°C | ISO 180/1U | NoBreak |
hardness | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
Rockwell hardness | R级 | ASTM D785 | 120 |
Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
Tensile modulus | ISO 527-2/1 | 2200 Mpa | |
elongation | 屈服 | ASTM D638 | 5.5 % |
tensile strength | 断裂 | ASTM D638 | 57.0 Mpa |
Tensile strain | 屈服 | ISO 527-2/50 | 6.0 % |
tensile strength | 断裂 | ISO 527-2/50 | 56.0 Mpa |
Flexural modulus | 50.0mm跨距 | ASTM D790 | 2280 Mpa |
tensile strength | 屈服 | ISO 527-2/50 | 61.0 Mpa |
Tensile modulus | ASTM D638 | 2300 Mpa | |
elongation | 断裂 | ASTM D638 | 110 % |
bending strength | 屈服,50.0mm跨距 | ASTM D790 | 100 Mpa |
ISO 178 | 90.0 Mpa | ||
Flexural modulus | ISO 178 | 2200 Mpa | |
tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
Tensile strain | 断裂 | ISO 527-2/50 | 100 % |
optical performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
Haze ratio | 2540µm | ASTM D1003 | <1.0 % |
refractive index | ASTM D542 | 1.582 | |
transmissivity | 2540µm | ASTM D1003 | 88.0 % |
flammability | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
UL flame retardant rating | 0.50mm | UL 94 | HB |
physical property | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
Shrinkage rate | MD:3.20mm | 内部方法 | 0.50-0.70 % |
Melt volume flow rate | 300°C/1.2kg | ISO 1133 | 51.0 cm3/10min |
Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.15 % |
饱和,23°C | ISO 62 | 0.30 % | |
melt mass-flow rate | 300°C/1.2kg | ASTM D1238 | 55 g/10min |
Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE NANSHA/HFD1910-NA9E108T |
---|---|---|---|
vicat | -- | ISO 306/B120 | 136 °C |
Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
TD:-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
Heat distortion temperature | 0.45MPa,未退火,3.20mm,HDT | ASTM D648 | 124 °C |
vicat | -- | ISO 306/B50 | 135 °C |
Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 8E-05 cm/cm/°C |
MD:-40到40°C | ISO 11359-2 | 8E-05 cm/cm/°C | |
Heat distortion temperature | 1.8MPa,Unannealed,64.0mmSpan,HDT | ISO 75-2/Af | 120 °C |
vicat | ASTM D152510 | 141 °C | |
Heat distortion temperature | 1.8MPa,未退火,3.20mm,HDT | ASTM D648 | 110 °C |
ball-indentation hardness | 125°C | IEC 60695-10-2 | Pass |