Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
POM K-2000 GY SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Automotive Applications
heat-resisting,high strength,Glass fiber reinforced
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/K-2000 GY |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 49 kJ/m² |
| Multi axis Instrumented Impact Energy | ISO 6603-2 | 0.820 J | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 6.5 kJ/m² |
| Dart impact | 23°C,EnergyatPeakLoad | ASTM D3763 | 6.41 J |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/K-2000 GY |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 87.0 °C |
| Linear coefficient of thermal expansion | TD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 159 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 110 °C | |
| Linear coefficient of thermal expansion | MD：-40到40°C | ISO 11359-2 | 1.1E-04 cm/cm/°C |
| MD：-40到40°C | ASTME831 | 1.1E-04 cm/cm/°C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/K-2000 GY |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 2070 Mpa | |
| elongation | 断裂 | ASTM D638 | 32 % |
| tensile strength | 屈服 | ASTM D638 | 55.5 Mpa |
| 屈服 | ISO 527-2 | 60.9 Mpa | |
| bending strength | ISO 178 | 65.6 Mpa | |
| Tensile strain | 屈服 | ISO 527-2 | 9.0 % |
| Wear factor | Washer | ASTM D3702Modified | 10.0 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Static | ASTM D3702Modified | 0.24 |
| flexural modulus | ASTM D790 | 2430 Mpa | |
| Tensile modulus | ISO 527-2/1 | 2560 Mpa | |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.38 |
| elongation | 屈服 | ASTM D638 | 9.3 % |
| Tensile strain | 断裂 | ISO 527-2 | 13 % |
| bending strength | ASTM D790 | 84.1 Mpa | |
| tensile strength | 断裂 | ASTM D638 | 51.8 Mpa |
| 断裂 | ISO 527-2 | 59.9 Mpa | |
| flexural modulus | ISO 178 | 2420 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/K-2000 GY |
|---|---|---|---|
| shrinkage rate | MD:24小时 | ISO 294-4 | 2.2 % |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.33 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 2.2 % |
| TD：24hr | ASTM D955 | 2.3 % | |
| TD:24小时 | ISO 294-4 | 2.1 % |