Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS XCM830-76701 SABIC INNOVATIVE US
CYCOLAC™
Automotive interior parts,Electrical applications
High mobility,High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 45 kJ/m² |
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 65.0 J |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 10 kJ/m² |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| bending strength | 屈服,50.0mm跨距4 | ASTM D790 | 95.0 Mpa |
| Tensile modulus | --2 | ASTM D638 | 3400 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 55.0 Mpa |
| elongation | 断裂3 | ASTM D638 | 100 % |
| tensile strength | 屈服3 | ASTM D638 | 60.0 Mpa |
| Flexural modulus | --5 | ISO 178 | 3100 Mpa |
| 50.0mm跨距4 | ASTM D790 | 3100 Mpa | |
| bending strength | --5,6 | ISO 178 | 95.0 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 5.0 % |
| tensile strength | 屈服 | ISO 527-2/5 | 56.0 Mpa |
| elongation | 屈服3 | ASTM D638 | 5.0 % |
| tensile strength | 断裂3 | ASTM D638 | 55.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 3100 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 100 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.70-0.80 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 11 g/10min |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.10 % |
| 饱和,23°C | ISO 62 | 0.40 % | |
| Melt volume flow rate | 260°C/5.0kg | ISO 1133 | 9.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/XCM830-76701 |
|---|---|---|---|
| thermal conductivity | ISO 8302 | 0.20 W/m/K | |
| vicat | -- | ISO 306/B120 | 140 °C |
| Linear coefficient of thermal expansion | TD:-40到40°C | ASTME831 | 7E-05 cm/cm/°C |
| vicat | -- | ASTMD152510 | 138 °C |
| Heat distortion temperature | 1.8MPa,未退火,64.0mm跨距9，HDT | ISO 75-2/Af | 118 °C |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 118 °C | |
| ball-indentation hardness | 125°C | IEC 60695-10-2 | 通过 |
| Linear coefficient of thermal expansion | MD:-40到40°C | ASTME831 | 6E-05 cm/cm/°C |