Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PBT 5201-X10 TORAY JAPAN
Toraycon®
Automotive sector,Electronic field,Electrical field
Flame retardant
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/5201-X10 |
|---|---|---|---|
| dielectric constant | ASTM D150/IEC 60250 | 3.4 | |
| Volume resistivity | ASTM D257/IEC 60093 | 2.0X10^14 Ω.cm |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/5201-X10 |
|---|---|---|---|
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 145 kg·cm/cm(J/M)ft·lb/in | |
| bending strength | ASTM D790/ISO 178 | 75 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | ASTM D790/ISO 178 | 2300 kg/cm²(MPa)[Lb/in²] | |
| elongation at break | ASTM D638/ISO 527 | >150 % | |
| Rockwell hardness | ASTM D785 | M72 | |
| tensile strength | ASTM D638/ISO 527 | 50 kg/cm²(MPa)[Lb/in²] |
| other | Test Condition | Test Method | TORAY JAPAN/5201-X10 |
|---|---|---|---|
| characteristic | 非增强高抗冲击级 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/5201-X10 |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.29 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.08 % |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/5201-X10 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | ASTM D648/ISO 75 | 56 ℃（℉） |
| Linear coefficient of thermal expansion | ASTM D696/ISO 11359 | 10.0X10^-5 mm/mm.℃ |