Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 53G33 B3378 ASAHI JAPAN
Leona™
Automotive Applications,Gears,water tank,Electrical/Electronic Applications,Application in the automotive field,component
high strength,High rigidity,Filler: Glass fiber reinf,33% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ASAHI JAPAN/53G33 B3378 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | ISO 179 | 92 kJ/m² |
| hardness | Test Condition | Test Method | ASAHI JAPAN/53G33 B3378 |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 121 |
| R级 | ASTM D785 | 121 | |
| M计秤 | ISO 2039-2 | 97 |
| Mechanical properties | Test Condition | Test Method | ASAHI JAPAN/53G33 B3378 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 4.0 % |
| bending strength | 23°C | ISO 178 | 296 Mpa |
| ASTM D790 | 309 Mpa | ||
| Flexural modulus | 23°C | ISO 178 | 9700 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 9500 Mpa |
| tensile strength | 断裂,23°C | ISO 527-2 | 203 Mpa |
| Flexural modulus | ASTM D790 | 8400 Mpa | |
| tensile strength | ASTM D638 | 215 Mpa |
| physical property | Test Condition | Test Method | ASAHI JAPAN/53G33 B3378 |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.30 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | -- % |
| Shrinkage rate | 吸水率(饱和,23°C) | 内部方法 | -- % |
| TD | 内部方法 | 0.90 % |
| Thermal performance | Test Condition | Test Method | ASAHI JAPAN/53G33 B3378 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 208 °C |
| thermal conductivity | 0.40 W/m/K | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 208 °C |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 2E-05 cm/cm/°C |