POM GC15 CELANESE USA
CELCON®
Automotive Applications,pipeline
enhance,toughness,copolymer,medial,Balanced,rigidity,Filler: Glass fiber reinf,15% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/GC15 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 4.9 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 5.3 kJ/m² |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/GC15 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 5950 Mpa | |
| Flexural modulus | 23°C | ISO 178 | 5850 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 91.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| tensile strength | 屈服,23°C | ASTM D638 | 85.5 Mpa |
| physical property | Test Condition | Test Method | CELANESE USA/GC15 |
|---|---|---|---|
| Shrinkage rate | MD | ASTM D955 | 0.40 % |
| TD | ISO 294-4 | 0.90 % | |
| MD | ISO 294-4 | 0.50 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| 饱和,23°C | ISO 62 | 0.80 % | |
| density | ASTM D792 | 1.54 g/cm³ | |
| Shrinkage rate | TD | ASTM D955 | 1.8 % |
| density | ISO 1183 | 1.50 g/cm³ |
| Thermal performance | Test Condition | Test Method | CELANESE USA/GC15 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 130 °C |
| melting temperature | ISO 11357-3 | 166 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 159 °C |
| melting temperature | ASTM D3418 | 165 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 4.6E-05 cm/cm/°C |
| TD | ISO 11359-2 | 1E-04 cm/cm/°C |