PBT 310SE0-BK SABIC INNOVATIVE US

VALOX™

Spool,Shell,switch,Home appliance components,Electronic field,Electrical field

Flame retardant

Plastic Datasheets

hardness	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Ball Pressure Test	H358/30	ISO 2039-1	105 Mpa
Rockwell hardness	R-Scale	ISO 2039-2	120

thermal performance	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Ball Pressure Test	125°C	IEC 60695-10-2	Pass
Hot deformation temperature	1.8MPa,Unannealed,3.20mm	ASTM D648	74.0 °C
		1.8MPa,Unannealed,6.40mm	ASTM D648	71.0 °C
		0.45MPa,Unannealed,6.40mm	ASTM D648	162 °C
		1.8MPa,Unannealed,64.0mmSpan13	ISO 75-2/Af	71.0 °C
		0.45MPa,Unannealed,100mmSpan	ISO 75-2/Be	135 °C
		1.8MPa,Unannealed,100mmSpan12	ISO 75-2/Ae	60.0 °C
Linear coefficient of thermal expansion	MD：-40to40°C	ASTME831	7.9E-05 cm/cm/°C
		TD：-40to40°C	ISO 11359-2	7.3E-05 cm/cm/°C
		TD：-40to40°C	ASTME831	7.9E-05 cm/cm/°C
		TD：23to60°C	ISO 11359-2	1E-04 cm/cm/°C
		MD：23to60°C	ISO 11359-2	1E-04 cm/cm/°C
		MD：-40to40°C	ISO 11359-2	7.6E-05 cm/cm/°C
		MD：60to138°C	ASTME831	1.3E-04 cm/cm/°C
RTI Elec		UL 746	120 °C
RTI Imp		UL 746	120 °C
RTI Str		UL 746	140 °C
thermal conductivity		ISO 8302	0.24 W/m/K
Vicat softening temperature		ASTM D152514	165 °C
		--	ISO 306/B120	165 °C
		--	ISO 306/B50	165 °C
		--	ISO 306/A50	212 °C

mechanical properties	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Bending modulus	50.0mmSpan	ASTM D790	2620 Mpa
Bending modulus			ISO 178	2600 Mpa
bending strength	Yield,50.0mmSpan	ASTM D790	101 Mpa
bending strength			ISO 178	90.0 Mpa
elongation	Break	ASTM D638	20 %
Taber abraser	1000Cycles,1000g,CS-17Wheel	Internal Method	19.0 mg
Tensile modulus		ASTM D638	2820 Mpa
Tensile modulus			ISO 527-2/1	2800 Mpa
Tensile strain	Yield	ASTM D638	20 %
		Break	ISO 527-2/50	20 %
		Yield	ISO 527-2/50	6.0 %
tensile strength	Yield	ASTM D638	58.0 Mpa
		Yield	ISO 527-2/50	55.0 Mpa
		Break	ISO 527-2/50	40.0 Mpa
		Break	ASTM D638	58.0 Mpa

Electrical performance	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Arc resistance		ASTM D495	PLC6
Compared to the anti leakage trace index	--	IEC 60112	PLC 3
		SolutionB	IEC 60112	PLC 4
		CTI	UL 746	PLC 3
Dielectric strength	3.20mm,in Oil	IEC 60243-1	15 KV/mm
		3.20mm,inAir	ASTM D149	18 KV/mm
		1.00mm15	IEC 60243-1	18 KV/mm
		1.60mm,in Oil	IEC 60243-1	24 KV/mm
		0.800mm,in Oil	IEC 60243-1	31 KV/mm
		1.60mm,in Oil	ASTM D149	22 KV/mm
Dissipation factor	1MHz	IEC 60250	0.010
		50Hz	IEC 60250	1E-03
		100Hz	IEC 60250	2E-03
		60Hz	IEC 60250	1E-03
High arc combustion index	HAI	UL 746	PLC 0
High voltage arc tracing rate	PLC	UL 746
High voltage arc tracing rate		HVTR	UL 746	PLC 4
Hot wire ignition	HWI	UL 746	PLC 2
Relative permittivity	100Hz	IEC 60250	3.10
		60Hz	IEC 60250	2.90
		50Hz	IEC 60250	2.90
		1MHz	IEC 60250	2.80
Surface resistivity		IEC 60093	>1.0E+15 ohms
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm

Physical properties	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
density		ISO 1183	1.40 g/cm³
density			ASTM D792	1.40 g/cm³
melt mass-flow rate	250°C/2.16kg	ASTM D1238	8.6 g/10min
Melt Volume Flow Rate (MVR)	250°C/2.16kg	ISO 1133	8.00 cm3/10min
Shrinkage rate	TD：--2	Internal Method	0.90-1.9 %
		MD：--4	Internal Method	0.90-1.6 %
		MD：3.20mm	Internal Method	1.5-2.3 %
		MD：--2	Internal Method	1.1-1.8 %
		MD：--3	Internal Method	1.5-2.3 %
		TD：--4	Internal Method	1.0-1.7 %
		TD：--3	Internal Method	1.6-2.4 %
Specific volume		ASTM D792	0.710 cm³/g
Water absorption rate	Equilibrium,23°C,50%RH	ISO 62	0.080 %
Water absorption rate		Saturation,23°C	ISO 62	0.36 %

impact performance	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Charpy Notched Impact Strength	23°C	ISO 179/2C	4.0 kJ/m²
		-30°C10	ISO 179/1eA	4.0 kJ/m²
		23°C10	ISO 179/1eA	8.0 kJ/m²
Dart impact	23°C,TotalEnergy	ASTM D3763	200 J
Impact strength of cantilever beam gap	23°C	ISO 180/1A	5.0 kJ/m²
		-30°C	ISO 180/1A	3.0 kJ/m²
		23°C	ASTM D256	37 J/m
		23°C	ASTM D4812	1600 J/m
		-30°C	ASTM D256	22 J/m
Impact strength of simply supported beam without notch	-30°C	ISO 179/1eU	NoBreak
Impact strength of simply supported beam without notch		23°C	ISO 179/1eU	NoBreak
Suspended wall beam without notch impact strength	-30°C	ISO 180/1U	NoBreak
Suspended wall beam without notch impact strength		23°C	ISO 180/1U	NoBreak

flammability	Test Condition	Test Method	SABIC INNOVATIVE US/310SE0-BK
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
Extreme Oxygen Index		ISO 4589-2	30 %
UL flame retardant rating	3.0mm	UL 94	5VA
UL flame retardant rating		0.71mm	UL 94	V-0