PPO/PA C82HL GRAY MITSUBISHI ENGINEERING JAPAN
LEMALLOY™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/C82HL GRAY |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | NoBreak |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/C82HL GRAY |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 93.0 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 62.0 Mpa |
| Tensile strain | 屈服,23°C | ISO 527-2 | 4.8 % |
| Flexural modulus | 23°C | ISO 178 | 2400 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| Nominal tensile fracture strain | 23°C | ISO 527-2 | 47 % |
| Electrical performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/C82HL GRAY |
|---|---|---|---|
| dielectric strength | 1.00mm | IEC 60243-1 | 33 KV/mm |
| Volume resistivity | IEC 60093 | 2E+15 ohms·cm | |
| Dissipation Factor | 100Hz | IEC 60250 | 5E-03 |
| relative permittivity | 100Hz | IEC 60250 | 3.40 |
| dielectric strength | 3.00mm | IEC 60243-1 | 18 KV/mm |
| relative permittivity | 1MHz | IEC 60250 | 3.20 |
| Surface Resistivity | IEC 60093 | 7E+14 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.012 |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/C82HL GRAY |
|---|---|---|---|
| Shrinkage rate | TD:3.20mm | 1.1-1.3 % | |
| MD:3.20mm | 1.1-1.3 % | ||
| Melt volume flow rate | 280°C/5.0kg | ISO 1133 | 115 cm3/10min |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/C82HL GRAY |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 165 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 70.0 °C |