Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS Rotec® ABS TS 12 ROMIRA GERMANY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ROMIRA GERMANY/Rotec® ABS TS 12 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 12 kJ/m² |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 70 kJ/m² |
| Mechanical properties | Test Condition | Test Method | ROMIRA GERMANY/Rotec® ABS TS 12 |
|---|---|---|---|
| Flexural modulus | 23°C | ISO 178 | 2700 MPa |
| tensile strength | 23°C | ISO 527-2/50 | 50.0 MPa |
| Tensile strain | 断裂,23°C | ISO 527-2/50 | 10 % |
| Tensile modulus | 23°C | ISO 527-2/1 | 2600 MPa |
| bending strength | 23°C | ISO 178 | 78.0 MPa |
| flammability | Test Condition | Test Method | ROMIRA GERMANY/Rotec® ABS TS 12 |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | ROMIRA GERMANY/Rotec® ABS TS 12 |
|---|---|---|---|
| Shrinkage rate | 23°C | ISO 294-4 | 0.30to0.70 % |
| density | 23°C | ISO 1183 | 1.05 g/cm³ |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.30 % |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 21 g/10min |
| Thermal performance | Test Condition | Test Method | ROMIRA GERMANY/Rotec® ABS TS 12 |
|---|---|---|---|
| thermal conductivity | DIN 52612 | 0.18 W/m/K | |
| Linear coefficient of thermal expansion | MD：23到55°C | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 80.0 °C |
| vicat | ISO 306/B50 | 100 °C |