PA12 55R53 SP 01 ARKEMA USA
Pebax®Rnew®
Automotive Applications、tubing
UV resistance、Thermal stability
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | -30°C | ISO 179/1eU | 无断裂 |
| 23°C | ISO 179/1eU | 无断裂 |
| hardness | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Supporting hardness | 邵氏 D, 15 秒 | ISO 7619-1 | 51 |
| Mechanical properties | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | -- Mpa | |
| Tensile stress | 断裂 | ISO 527-2 | 45.0 Mpa |
| Tensile strain | 断裂 | ISO 527-2 | > 300 % |
| Tensile stress | 50% 应变 | ISO 527-2 | -- Mpa |
| squeeze out | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| drying temperature | 65 到 75 °C | ||
| drying time | 4.0 到 8.0 hr | ||
| Melt Temperature | 200 到 270 °C |
| physical property | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C, 50% RH | ISO 62 | 0.70 % |
| Shrinkage rate | 流量 | ISO 294-4 | 1.0 % |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.5 % |
| Shrinkage rate | 横向流量 | ISO 294-4 | 1.0 % |
| Thermal performance | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Melting temperature 2 | ISO 11357-3 | 167 °C | |
| vicat | ISO 306/B50 | 156 °C | |
| Melting temperature 2 | Renewable Carbon Conent | CSA LISTED | 62 到 66 % |
| injection | Test Condition | Test Method | ARKEMA USA/55R53 SP 01 |
|---|---|---|---|
| Temperature | 25 到 60 °C | ||
| Processing (melt) temperature | 210 到 230 °C | ||
| drying temperature | 65 到 75 °C | ||
| drying time | 4.0 到 8.0 hr |