Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC A 8000 NATURALE SO.F.TER ITALY
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 90 J/m |
| -30°C | ASTM D256 | 350 J/m | |
| 0°C | ASTM D256 | 400 J/m |
| Electrical performance | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 |
| Mechanical properties | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 2.0 % |
| Flexural modulus | ASTM D790 | 2350 MPa | |
| tensile strength | 屈服 | ASTM D638 | 60.0 MPa |
| flammability | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| Hot filament ignition temperature | IEC 60695-2-13 | 750 °C | |
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 1.6mm | UL 94 | HB | |
| Limiting Oxygen Index | ASTM D2863 | 23 % |
| physical property | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.55 % | |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 12 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.10 % |
| density | ASTM D792 | 1.15 g/cm³ |
| Thermal performance | Test Condition | Test Method | SO.F.TER ITALY/ A 8000 NATURALE |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 110 °C |
| ball-indentation hardness | 125°C | IEC 335 | 通过 |
| vicat | ASTM D15252 | 110 °C |