Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC/ABS 8800 SABIC INNOVATIVE US
CYCOLAC™
Automotive sector
heat-resisting、High impact resistance
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | SABIC INNOVATIVE US/8800 |
|---|---|---|---|
| Linear thermal expansion coefficient | TD：-40到40°C | ISO11359-2 | 7E-05 cm/cm/°C |
| Vicat Softening Temperature | -- | ISO306/B50 | 135 °C |
| Linear thermal expansion coefficient | MD：-40到40°C | ISO11359-2 | 6E-05 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距 | ISO75-2/Af | 118 °C |
| Vicat Softening Temperature | -- | ISO306/B120 | 137 °C |
| Physical | Test Condition | Test Method | SABIC INNOVATIVE US/8800 |
|---|---|---|---|
| Moisture Absorption | 平衡,23°C,50%RH | ISO62 | 0.10 % |
| Modeling Shrinkage | MD：3.20mm | 内部方法 | 0.40to0.60 % |
| Melt Volume flow Rate | 265°C/5.0kg | ISO1133 | 10.0 cm3/10min |
| Moisture Absorption | 饱和,23°C | ISO62 | 0.40 % |
| Mechanical Properties | Test Condition | Test Method | SABIC INNOVATIVE US/8800 |
|---|---|---|---|
| Flexural Modulus | ISO178 | 3100 Mpa | |
| Tensile Strain | 断裂 | ISO527-2/5 | 100 % |
| Tensile Modulus | ISO527-2/1 | 3200 Mpa | |
| Flexural Stress | ISO178 | 95.0 Mpa | |
| Tensile Stress | 断裂 | ISO527-2/5 | 58.0 Mpa |
| Tensile Strain | 屈服 | 4.2 % | |
| Tensile Stress | 55.0 Mpa |
| Impact Properties | Test Condition | Test Method | SABIC INNOVATIVE US/8800 |
|---|---|---|---|
| Notched Izod Impact Strength | -30°C | ISO180/1A | 10 kJ/m² |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 35 kJ/m² |
| Notched Izod Impact Strength | ISO180/1A | 30 kJ/m² |