Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
COC APL5014CL MITSUI CHEM JAPAN
APEL™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| Suspended wall beam without notch impact strength | ASTM D256 | 10.0 kJ/m² |
| film | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| Water Vapor Transmission Rate | ASTMF1249 | 0.090 g·mm/m²/atm/24hr |
| Mechanical properties | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 3.0 % |
| bending strength | ASTM D790 | 100 Mpa | |
| tensile strength | 屈服 | ASTM D638 | 60.0 Mpa |
| Flexural modulus | ASTM D790 | 3200 Mpa |
| optical performance | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| transmissivity | ASTM D1003 | 90.0 % | |
| refractive index | ASTM D542 | 1.540 | |
| Haze ratio | ASTM D1003 | <0.50 % |
| physical property | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| Shrinkage rate | MD | 内部方法 | 0.60 % |
| melt mass-flow rate | 260°C/2.16kg | ASTM D1238 | 36 g/10min |
| Shrinkage rate | TD | 内部方法 | 0.50 % |
| Thermal performance | Test Condition | Test Method | MITSUI CHEM JAPAN/APL5014CL |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火，HDT | ASTM D648 | 125 °C |
| Linear coefficient of thermal expansion | TD | ASTM D696 | 6E-05 cm/cm/°C |
| Glass Transition Temperature | 内部方法 | 135 °C | |
| Linear coefficient of thermal expansion | MD | ASTM D696 | 7E-05 cm/cm/°C |