PC LUX7632C-WH7E317X SABIC INNOVATIVE US
LEXAN™ 
Plastic bag、Lighting applications
Flame retardant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--

Plastic Datasheets

Impact resistanceTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
Charpy Notched Impact Strength23°CISO 179/1eA10 kJ/m²
Impact strength of simply supported beam without notch-30°CISO 179/1eU无断裂
Suspended wall beam without notch impact strength-30°CASTM D4812无断裂
Charpy Notched Impact Strength-30°CISO 179/1eA9.0 kJ/m²
Impact strength of simply supported beam without notch23°CISO 179/1eU无断裂
Dart impact23°C, Total EnergyASTM D376366.0 J
Suspended wall beam without notch impact strength23°CASTM D4812无断裂
Mechanical propertiesTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
Tensile modulus--2ASTM D6382500 Mpa
tensile strength 屈服3ASTM D63868.0 Mpa
elongation断裂3ASTM D63851 %
断裂ISO 527-2/5023 %
Flexural modulus--5ISO 1782500 Mpa
bending strength屈服, 50.0 mm 跨距4ASTM D790106 Mpa
--5,6ISO 178103 Mpa
Flexural modulus50.0 mm 跨距4ASTM D7902400 Mpa
tensile strength 断裂ISO 527-2/5052.0 Mpa
屈服ISO 527-2/5067.0 Mpa
elongation屈服ISO 527-2/506.0 %
屈服3ASTM D6386.0 %
tensile strength 断裂3ASTM D63852.0 Mpa
Tensile modulus--ISO 527-2/12400 Mpa
Electrical performanceTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
Dissipation Factor1.10 GHzASTM ES7-835.8E-3
dielectric constant1.10 GHzASTM ES7-832.79
flammabilityTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
UL flame retardant rating3.0 mmUL 945VA
1.0 mmUL 94V-0
0.40 mmUL 94V-2
Hot filament ignition temperature1.0 mmIEC 60695-2-13875 °C
Burning wire flammability index1.0 mmIEC 60695-2-12960 °C
physical property Test ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
Water absorption rate平衡, 23°C, 50% RHISO 620.11 %
Shrinkage rate横向流动 : 3.20 mm内部方法0.60 - 0.80 %
Melt volume flow rate300°C/1.2 kgISO 11335.00 cm3/10min
Outdoor applicabilityUL 746Cf1
melt mass-flow rate300°C/1.2 kgASTM D12385.0 g/10 min
Shrinkage rate流动 : 3.20 mm内部方法0.55 - 0.75 %
Water absorption rate饱和, 23°CISO 620.14 %
Thermal performanceTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
Linear coefficient of thermal expansion流动 : -40 到 40°CASTM E8316.6E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDTISO 75-2/Ae120 °C
Linear coefficient of thermal expansion横向 : 23 到 80°CISO 11359-27.6E-5 cm/cm/°C
流动 : 23 到 80°CISO 11359-27.2E-5 cm/cm/°C
Heat distortion temperature0.45 MPa, 未退火, 3.20 mm，HDTASTM D648131 °C
ball-indentation hardness123 到 127°CIEC 60695-10-2通过
RTIUL 746125 °C
vicat--ISO 306/B120139 °C
--ASTM D152510136 °C
--ISO 306/B50137 °C
Heat distortion temperature0.45 MPa, 未退火, 4.00 mm, 100 mm 跨距9，HDTISO 75-2/Be131 °C
RTI ImpUL 746120 °C
Linear coefficient of thermal expansion横向 : -40 到 40°CASTM E8317.0E-5 cm/cm/°C
Heat distortion temperature1.8 MPa, 未退火, 3.20 mm，HDTASTM D648120 °C
RTI ElecUL 746125 °C
injectionTest ConditionTest MethodSABIC INNOVATIVE US/LUX7632C-WH7E317X
screw speed40 to 70 rpm
Suggested maximum moisture content0.020 %
Processing (melt) temperature290 to 310 °C
drying temperature120 °C
Suggested injection volume40 to 60 %
drying time3.0 to 4.0 hr
Temperature in the middle of the barrel275 to 300 °C
Temperature at the rear of the barrel265 to 290 °C
Exhaust hole depth0.025 to 0.076 mm
Temperature at the front of the material cylinder290 to 310 °C
Back pressure0.300 to 0.700 Mpa
Temperature70 to 95 °C
Spray nozzle temperature280 to 305 °C