Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
HDPE Polifil® PE RP-HDPE 美国The Plastics
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | 美国The Plastics/Polifil® PE RP-HDPE |
|---|---|---|---|
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 85 J/m |
| Dart impact | 23°C,12.7mm | ASTM D3029 | >22.6 J |
| hardness | Test Condition | Test Method | 美国The Plastics/Polifil® PE RP-HDPE |
|---|---|---|---|
| Hardness (Shore) | 邵氏D | ASTM D1415 | 64 |
| Mechanical properties | Test Condition | Test Method | 美国The Plastics/Polifil® PE RP-HDPE |
|---|---|---|---|
| bending strength | 23°C | ASTM D790 | 27.6 MPa |
| tensile strength | 23°C | ASTM D638 | 24.1 MPa |
| Tensile modulus | 23°C | ASTM D638 | 1170 MPa |
| Flexural modulus | 23°C | ASTM D790 | 1030 MPa |
| elongation | 屈服,23°C | ASTM D638 | 12 % |
| 断裂,23°C | ASTM D638 | >200 % |
| physical property | Test Condition | Test Method | 美国The Plastics/Polifil® PE RP-HDPE |
|---|---|---|---|
| density | ASTM D792 | 0.958 g/cm³ | |
| Shrinkage rate | MD：3.18mm | ASTM D955 | 2.8 % |
| melt mass-flow rate | 190°C/2.16kg | ASTM D1238 | 0.10to5.0 g/10min |
| Thermal performance | Test Condition | Test Method | 美国The Plastics/Polifil® PE RP-HDPE |
|---|---|---|---|
| Hot deformation temperature (HDT) | 1.8MPa,未退火，HDT | ASTM D648 | 32.2 °C |
| 0.45MPa,未退火，HDT | ASTM D648 | 71.1 °C |