Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PS SECCO HIPS-622S Shanghai SECCO Petrochemical Co., Ltd
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 11 kJ/m² |
| hardness | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| Rockwell hardness | R计秤 | ISO 2039-2 | 97 |
| Mechanical properties | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| Flexural modulus | ISO 178 | 1650 MPa | |
| Nominal tensile fracture strain | ISO 527-2/50 | 60 % | |
| bending strength | ISO 178 | 40.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 26.0 MPa |
| 断裂 | ISO 527-2/50 | 25.0 MPa |
| flammability | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| melt mass-flow rate | 200°C/5.0kg | ISO 1133 | 3.6 g/10min |
| Shrinkage rate | 24小时 | ISO 294-4 | 0.40to0.60 % |
| Water absorption rate | 饱和,23°C | ISO 62 | <0.10 % |
| density | ISO 1183 | 1.04 g/cm³ |
| Thermal performance | Test Condition | Test Method | Shanghai SECCO Petrochemical Co., Ltd/SECCO HIPS-622S |
|---|---|---|---|
| vicat | ISO 306/B50 | 90.0 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 72.0 °C |