POM KL-4030 EM SABIC INNOVATIVE US
LNP™ LUBRICOMP™
Plastic bag,Medical and nursing supplies
Low extract,wear resistant
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4030 EM |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 46 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ISO 180/1A | 3.0 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4030 EM |
|---|---|---|---|
| Linear coefficient of thermal expansion | TD：-30to30°C | ASTM D696 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 88.0 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 158 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 97.0 °C | |
| Linear coefficient of thermal expansion | MD：-30到30°C | ASTM D696 | 1.1E-04 cm/cm/°C |
| Heat Deflection Temperature | 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 149 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4030 EM |
|---|---|---|---|
| Tensile strain | 断裂 | ISO 527-2/5 | 16 % |
| tensile strength | 断裂 | ISO 527-2/5 | 46.0 Mpa |
| Tensile modulus | ASTM D638 | 2530 Mpa | |
| elongation | 断裂 | ASTM D638 | 19 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 2210 Mpa |
| tensile strength | 屈服 | ASTM D638 | 48.0 Mpa |
| Wear factor | Ring | ASTM D3702Modified | 0.300 10^-10in^5-min/ft-lb-hr |
| tensile strength | 屈服 | ISO 527-2/5 | 46.0 Mpa |
| Wear factor | Washer | ASTM D3702Modified | 11.0 10^-10in^5-min/ft-lb-hr |
| coefficient of friction | Static | ASTM D3702Modified | 0.17 |
| Tensile modulus | ISO 527-2/1 | 2460 Mpa | |
| Tensile strain | 屈服 | ISO 527-2/5 | 9.0 % |
| coefficient of friction | Dynamic | ASTM D3702Modified | 0.35 |
| elongation | 屈服 | ASTM D638 | 10 % |
| tensile strength | 断裂 | ASTM D638 | 48.0 Mpa |
| bending strength | ASTM D790 | 75.8 Mpa | |
| flexural modulus | ISO 178 | 2250 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/KL-4030 EM |
|---|---|---|---|
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.20 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 1.0-3.0 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.29 % |
| shrinkage rate | TD：24hr | ASTM D955 | 1.0-3.0 % |