PBT 3316HR BK CELANESE USA
CELANEX®
Automotive sector,Electronic and electrical accessories
Glass fiber reinforced,Filler: Glass fiber reinf,30% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| thermal performance | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 202 °C |
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 9E-05 cm/cm/°C |
| melting temperature | ISO 11357-3 | 225 °C | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |
| Electrical performance | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | IEC 60112 | PLC 2 | |
| ASTM D3638 | PLC 2 | ||
| volume resistivity | IEC 60093 | 1E+15 ohms·cm | |
| ASTM D257 | 4.4E+16 ohms·cm | ||
| relative permittivity | 1MHz | IEC 60250 | 2.90 |
| Surface Resistivity | IEC 60093 | 1E+15 ohms | |
| Dissipation Factor | 1MHz | IEC 60250 | 0.015 |
| Mechanical properties | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| flexural modulus | 23°C | ISO 178 | 8950 Mpa |
| Tensile modulus | ISO 527-2/1A/1 | 9850 Mpa | |
| bending strength | 23°C | ISO 178 | 175 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.5 % |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 115 Mpa |
| Physical properties | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| density | ISO 1183 | 1.61 g/cm³ | |
| shrinkage rate | TD | ISO 294-4 | 0.80-1.3 % |
| MD | ISO 294-4 | 0.10-0.80 % |
| flammability | Test Condition | Test Method | CELANESE USA/3316HR BK |
|---|---|---|---|
| UL flame retardant rating | 0.75mm | UL 94 | V-0 |