PC+ABS Kinta HI5603 Kinta Technology (Hong Kong) Co., Ltd.
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| Impact strength of cantilever beam gap | -30°C,3.20mm | ASTM D256 | 20.0 kJ/m² |
| 23°C,3.20mm | ASTM D256 | 40.0 kJ/m² |
| hardness | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| Rockwell hardness | R级 | ASTM D785 | 118 |
| Electrical performance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| Volume resistivity | ASTM D257 | 1E+18 ohms·cm |
| Mechanical properties | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 50 % |
| tensile strength | ASTM D638 | 48.0 MPa | |
| Flexural modulus | ASTM D790 | 2100 MPa | |
| bending strength | ASTM D790 | 78.0 MPa |
| flammability | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| Shrinkage rate | MD：3.00mm | ASTM D955 | 0.60to0.80 % |
| melt mass-flow rate | 260°C/5.0kg | ASTM D1238 | 14 g/10min |
| Water absorption rate | 23°C,24hr | ASTM D570 | 0.70 % |
| density | ASTM D792 | 1.10 g/cm³ |
| Thermal performance | Test Condition | Test Method | Kinta Technology (Hong Kong) Co., Ltd./Kinta HI5603 |
|---|---|---|---|
| Linear coefficient of thermal expansion | MD | ASTM D696 | 8E-05 cm/cm/°C |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 95.0 °C |