PPO IGN320-111 SABIC INNOVATIVE US
NORYL™
Automotive interior parts、Electrical applications、Application in the automo
High temperature resistan、High mobility、Glass fiber reinforced、Filler: Glass fiber reinf、20% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/IGN320-111 |
|---|---|---|---|
| Dart impact | 23°C,TotalEnergy | ASTM D3763 | 16.5 J |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/IGN320-111 |
|---|---|---|---|
| dielectric strength | 1.60mm,inOil | ASTM D149 | 34 KV/mm |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/IGN320-111 |
|---|---|---|---|
| Tensile modulus | ASTM D638 | 6260 Mpa | |
| elongation | 断裂 | ASTM D638 | 2.4 % |
| tensile strength | 断裂 | ASTM D638 | 109 Mpa |
| 屈服 | ASTM D638 | 109 Mpa | |
| Flexural modulus | 50.0mm跨距 | ASTM D790 | 5720 Mpa |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 170 Mpa |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/IGN320-111 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | 内部方法 | 0.10-0.30 % |
| melt mass-flow rate | 300°C/5.0kg | ASTM D1238 | 13 g/10min |
| Shrinkage rate | TD：3.20mm | 内部方法 | 0.20-0.40 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/IGN320-111 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 164 °C |
| vicat | ASTM D15255 | 175 °C | |
| Heat distortion temperature | 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 159 °C |