PPA NILAMID® XT4 GF30 Celanese Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 8.5 kJ/m² |
| -30°C | ISO 179/1eA | 7.5 kJ/m² | |
| Impact strength of simply supported beam without notch | 23°C | ISO 179/1eU | 35 kJ/m² |
| -30°C | ISO 179/1eU | 32 kJ/m² | |
| Impact strength of cantilever beam gap | 23°C | ISO 180/A | 8.0 kJ/m² |
| Mechanical properties | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.5 % |
| Tensile modulus | 23°C | ISO 527-2 | 12000 MPa |
| tensile strength | 屈服,23°C | ISO 527-2 | 150 MPa |
| Electrical performance | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| Compared to the Leakage Tracking Index (CTI) | 3.20mm,解决方案A | IEC 60112 | PLC 1 |
| Volume resistivity | 23°C | IEC 60093 | 1E+15 ohms·cm |
| dielectric strength | 2.00mm | IEC 60243-1 | 21 kV/mm |
| flammability | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| UL flame retardant rating | 3.2mm | UL 94 | HB |
| 0.8mm | UL 94 | HB | |
| 1.6mm | UL 94 | HB | |
| 0.40mm | UL 94 | HB |
| physical property | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| density | 23°C | ISO 1183 | 1.43 g/cm³ |
| Shrinkage rate | TD:23°C | ISO 294-4 | 0.70 % |
| MD:23°C | ISO 294-4 | 0.30 % | |
| Water absorption rate | 饱和,23°C | ISO 62 | 0.10 % |
| Thermal performance | Test Condition | Test Method | Celanese Corporation/NILAMID® XT4 GF30 |
|---|---|---|---|
| Continuous use temperature | IEC 60216 | 140 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 295 °C |