PBT A GB 20 A SCHULMAN USA
SCHULADUR®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Thermal Properties | Test Condition | Test Method | A SCHULMAN USA/A GB 20 |
|---|---|---|---|
| Vicat Softening Temperature | ISO306/A50 | 218 °C | |
| Heat Deflection Temperature | 0.45MPa未退火 | ISO75-2/Bf | 175 °C |
| Vicat Softening Temperature | ISO306/B50 | 184 °C | |
| Heat Deflection Temperature | 1.80MPa退火 | ISO75-2/Af | 94 °C |
| Hardness | Test Condition | Test Method | A SCHULMAN USA/A GB 20 |
|---|---|---|---|
| Ball Indentation Hardness | ISO2039-1 | 113 Mpa |
| Mechanical Properties | Test Condition | Test Method | A SCHULMAN USA/A GB 20 |
|---|---|---|---|
| Tensile Elongation?(Break) | 23°C | ISO527-2 | 6.00 % |
| Flexural Strength | 23°C | ISO178 | 83 Mpa |
| Charpy Unnotched Impact Strength | -30°C | ISO179/1eU | 30 kJ/m² |
| Flexural Modulus | 23°C | ISO178 | 3300 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO179/1eA | 3.5 kJ/m² |
| Tensile Strength | 23°C | ISO527-2 | 50 Mpa |
| Tensile Modulus | 23°C | ISO527-2 | 3400 Mpa |
| Charpy Notched Impact Strength | 23°C | ISO179/1eA | 5.0 kJ/m² |
| Charpy Unnotched Impact Strength | 23°C | ISO179/1eU | 50 kJ/m² |
| Physical | Test Condition | Test Method | A SCHULMAN USA/A GB 20 |
|---|---|---|---|
| Melt Mass-Flow Rate | 250℃/2.16Kg | ISO1133 | 15.0 cm3/10min |
| Flammability | Test Condition | Test Method | A SCHULMAN USA/A GB 20 |
|---|---|---|---|
| Glow Wire Ignition Temperature | 3.00mm | IEC60695-2-13 | 750 °C |
| Fire rating | UL-94 | 3.20mm HB | |
| Glow Wire Ignition Temperature | 1.50mm | IEC60695-2-13 | 750 °C |
| 3.00mm | IEC60695-2-12 | 725 °C | |
| 1.50mm | IEC60695-2-12 | 725 °C |