PBT 6400-2 CELANESE USA
--
Electronic and electrical accessories,Automotive sector
Excellent appearance,Bending resistance,Filler: Glass mineral,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | CELANESE USA/6400-2 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1A/1 | 12000 Mpa | |
| bending strength | 23°C | ISO 178 | 180 Mpa |
| Flexural modulus | 23°C | ISO 178 | 11000 Mpa |
| tensile strength | 断裂 | ISO 527-2/1A/5 | 110 Mpa |
| Tensile strain | 断裂 | ISO 527-2/1A/5 | 2.0 % |
| physical property | Test Condition | Test Method | CELANESE USA/6400-2 |
|---|---|---|---|
| Shrinkage rate | MD | ISO 294-4 | 0.40-0.60 % |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.20 % |
| Thermal performance | Test Condition | Test Method | CELANESE USA/6400-2 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 220 °C |
| vicat | ISO 306/B50 | 220 °C | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 200 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.5E-05 cm/cm/°C |