Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PEI HU1000-7HD395 SABIC INNOVATIVE US
ULTEM™
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ASTM D4812 | 1300 J/m |
| Dart impact | 23°C, Total Energy | ASTM D3763 | 0.00 J |
| Mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Tensile modulus | --2 | ASTM D638 | 3580 Mpa |
| tensile strength | 断裂 | ISO 527-2/5 | 85.0 Mpa |
| 屈服3 | ASTM D638 | 110 Mpa | |
| elongation | 断裂3 | ASTM D638 | 60 % |
| Flexural modulus | --5 | ISO 178 | 3300 Mpa |
| bending strength | 屈服, 50.0 mm 跨距4 | ASTM D790 | 173 Mpa |
| --5,6 | ISO 178 | 160 Mpa | |
| Flexural modulus | 50.0 mm 跨距4 | ASTM D790 | 3430 Mpa |
| elongation | 屈服 | ISO 527-2/5 | 6.0 % |
| tensile strength | 屈服 | ISO 527-2/5 | 105 Mpa |
| elongation | 屈服3 | ASTM D638 | 7.0 % |
| tensile strength | 断裂3 | ASTM D638 | 90.0 Mpa |
| Tensile modulus | -- | ISO 527-2/1 | 3200 Mpa |
| elongation | 断裂 | ISO 527-2/5 | 60 % |
| Electrical performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Dissipation Factor | 1 kHz | ASTM D150 | 1.3E-3 |
| dielectric strength | 1.60 mm, in Oil | ASTM D149 | 28 KV/mm |
| Volume resistivity | ASTM D257 | 1.0E+17 ohms·cm | |
| Dissipation Factor | 2.45 GHz | ASTM D150 | 2.5E-3 |
| dielectric strength | 1.60 mm, in Air | ASTM D149 | 33 KV/mm |
| Hot wire ignition (HWI) | UL 746 | PLC 1 | |
| dielectric constant | 1 kHz | ASTM D150 | 3.15 |
| arc resistance | ASTM D495 | PLC 5 | |
| High Voltage Arc Traceability Rate (HVTR) | UL 746 | PLC 2 | |
| Compared to the Leakage Tracking Index (CTI) | UL 746 | PLC 4 | |
| High arc combustion index (HAI) | UL 746 | PLC 3 |
| flammability | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Limiting Oxygen Index | ASTM D2863 | 47 % |
| physical property | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| Water absorption rate | 平衡, 23°C | ASTM D570 | 1.3 % |
| 平衡, 23°C, 50% RH | ISO 62 | 0.70 % | |
| 24 hr | ASTM D570 | 0.25 % | |
| melt mass-flow rate | 337°C/6.6 kg | ASTM D1238 | 9.0 g/10 min |
| Melt volume flow rate | 220°C/5.0 kg | ISO 1133 | 13.0 cm3/10min |
| Water absorption rate | 饱和, 23°C | ISO 62 | 1.3 % |
| Shrinkage rate | 3.20 mm，Flow | 内部方法 | 0.50 - 0.70 % |
| Thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| vicat | -- | ISO 306/B120 | 211 °C |
| Linear coefficient of thermal expansion | 流动 : -20 到 150°C | ASTM E831 | 5.6E-5 cm/cm/°C |
| vicat | -- | ASTM D15259 | 218 °C |
| Linear coefficient of thermal expansion | 横向 : -20 到 150°C | ASTM E831 | 5.4E-5 cm/cm/°C |
| 横向 : -40°C | ISO 11359-2 | 5.0E-5 cm/cm/°C | |
| vicat | -- | ISO 306/B50 | 215 °C |
| Linear coefficient of thermal expansion | 流动 : -40 到 40°C | ISO 11359-2 | 5.0E-5 cm/cm/°C |
| Heat distortion temperature | 1.8 MPa, 未退火, 6.40 mm，HDT | ASTM D648 | 201 °C |
| 1.8 MPa, 未退火, 4.00 mm, 64.0 mm 跨距8，HDT | ISO 75-2/Af | 215 °C |
| injection | Test Condition | Test Method | SABIC INNOVATIVE US/HU1000-7HD395 |
|---|---|---|---|
| screw speed | 40 to 70 rpm | ||
| Suggested maximum moisture content | 0.020 % | ||
| Processing (melt) temperature | 350 to 400 °C | ||
| drying temperature | 150 °C | ||
| Suggested injection volume | 40 to 60 % | ||
| drying time | 4.0 to 6.0 hr | ||
| Temperature in the middle of the barrel | 340 to 400 °C | ||
| Temperature at the rear of the barrel | 330 to 400 °C | ||
| Exhaust hole depth | 0.025 to 0.076 mm | ||
| Temperature at the front of the material cylinder | 345 to 400 °C | ||
| Back pressure | 0.300 to 0.700 Mpa | ||
| Temperature | 135 to 165 °C | ||
| Spray nozzle temperature | 345 to 400 °C |