Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 920 555 IS002 TORAY MALAYSIA
Toyolac®
small home appliances、Electronic field
High rigidity、transparent
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ASTM D785 | 115 |
| R计秤,23°C | ISO 2039-2 | 115 |
| Mechanical properties | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 20 % |
| Tensile strain | 断裂,23°C | ISO 527-2 | 17 % |
| bending strength | 23°C | ISO 178 | 77.0 Mpa |
| ASTM D790 | 74.0 Mpa | ||
| tensile strength | 屈服,23°C | ISO 527-2 | 54.0 Mpa |
| Flexural modulus | 23°C | ISO 178 | 2260 Mpa |
| ASTM D790 | 2160 Mpa | ||
| tensile strength | ASTM D638 | 48.0 Mpa |
| optical performance | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| Haze ratio | 3000µm | ISO 14782 | 2.0 % |
| transmissivity | 总计,3000µm | ISO 13468 | 88.0 % |
| flammability | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| UL flame retardant rating | UL 94 | HB |
| physical property | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| Shrinkage rate | 内部方法 | 0.40-0.60 % | |
| melt mass-flow rate | 220°C/10.0kg | ISO 1133 | 25 g/10min |
| Thermal performance | Test Condition | Test Method | TORAY MALAYSIA/920 555 IS002 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 83.0 °C |
| vicat | 90.0 °C | ||
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 77.0 °C |