ABS PA-77NB TAIWAN CHIMEI
POLYLAC®
small home appliances,Automotive sector
High temperature resistan
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
thermal performance | Test Condition | Test Method | TAIWAN CHIMEI/PA-77NB |
---|---|---|---|
Hot deformation temperature | 1.8MPa,Unannealed | ISO 75/A | 86 °C |
Linear coefficient of thermal expansion | 燃烧等级,1.5mm | UL 94 | HB |
ISO 11359 | 8.4×10-5 | ||
Vicat softening temperature | 1kg,50℃/hr | ISO 306 | 115 °C |
mechanical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-77NB |
---|---|---|---|
Bending modulus | 2mm/min | ISO 178 | 2.2 GPa |
bending strength | 2mm/min | ISO 178 | 70 Mpa |
Charpy Notched Impact Strength | 23℃,Notched | ISO 179 | 21 kJ/m² |
Elongation at Break | 50mm/min,Break | ISO 527 | 50 % |
Impact strength of cantilever beam gap | 23℃,Notched | ISO 180/1A | 23 kJ/m² |
tensile strength | 50mm/min,Yield | ISO 527 | 45 Mpa |
Physical properties | Test Condition | Test Method | TAIWAN CHIMEI/PA-77NB |
---|---|---|---|
melt mass-flow rate | 220℃×10kg | ISO 1133 | 10 |
Shrinkage rate | ISO 294-4 | 0.3-0.6 % |