POM Copolymer CA3899 Cabot Corporation
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
Impact resistance | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
Impact strength of cantilever beam gap | 23°C | ISO 180 | 11 kJ/m² |
hardness | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
Shore hardness | 邵氏D,15秒 | ASTM D2240 | 79 |
Electrical performance | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
Surface Resistivity | 内部方法 | 5E+02 ohms | |
Volume resistivity | 内部方法 | 39 ohms·cm |
Mechanical properties | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
tensile strength | 断裂 | ISO 527-2 | 45.2 MPa |
Tensile strain | 断裂 | ISO 527-2 | 42 % |
tensile strength | 屈服 | ISO 527-2 | 45.7 MPa |
Flexural modulus | ISO 178 | 1900 MPa |
physical property | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
melt mass-flow rate | 190°C/5.0kg | ISO 1133 | 9.3 g/10min |
Shrinkage rate | MD | ASTM D955 | 1.5to2.5 % |
melt mass-flow rate | 190°C/10.0kg | ISO 1133 | 28 g/10min |
density | 23°C | 内部方法 | 1.39 g/cm³ |
melt mass-flow rate | 190°C/2.16kg | ISO 1133 | 3.0 g/10min |
Thermal performance | Test Condition | Test Method | Cabot Corporation/ CA3899 |
---|---|---|---|
Heat distortion temperature | 1.8MPa,未退火,HDT | ISO 75-2/A | 72.0 °C |
vicat | ISO 306/A | 168 °C |