Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
ABS 3001G UMG JAPAN
UMG ABS®
--
--
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| Rockwell hardness | R计秤,23°C | ISO 2039-2 | 109 |
| Basic performance | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| melt mass-flow rate | 5 g/10min |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| Charpy Notched Impact Strength | 28 kJ/m² | ||
| Flexural modulus | ASTM D790/ISO 178 | 2.600 kg/cm²(MPa)[Lb/in²] | |
| bending strength | 23°C | ISO 178 | 72.0 Mpa |
| Flexural modulus | 2600 Mpa | ||
| 23°C | ISO 178 | 2600 Mpa | |
| Tensile modulus | 23°C | ISO 527-2 | 2350 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 28 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 23°C | ISO 527-2 | 45.0 Mpa |
| other | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| characteristic | 抗疲劳 |
| Physical properties | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| melt mass-flow rate | ASTM D1238/ISO 1133 | 5 g/10min |
| flammability | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| UL flame retardant rating | 1.5mm | UL 94 | HB |
| physical property | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| Shrinkage rate | MD：23°C | ISO 294-4 | 0.40-0.60 % |
| Melt volume flow rate | 220°C/10.0kg | ISO 1133 | 5.00 cm3/10min |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/3001G |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | HDT | 83 °C | |
| 1.8MPa,未退火，HDT | ISO 75-2/Af | 83.0 °C | |
| HDT | ASTM D648/ISO 75 | 83 ℃（℉） | |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 8.5E-05 cm/cm/°C |
| UL flame retardant rating | UL 94 | HB |