PC GN-3620L PC vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Reference Price

PC TEIJIN JAPAN GN-3620L

US$ 3,830 / MT

FOB Shenzhen Port

mechanical properties	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
bending strength		ISO 178	138 Mpa
Tensile strain	Break	ISO 527-2/5	1.0 %
bending strength		ASTM D790/ISO 178	138 kg/cm²(MPa)[Lb/in²]
Bending modulus		ISO 178	5600 Mpa
Bending modulus			ASTM D790/ISO 178	5600 kg/cm²(MPa)[Lb/in²]
Tensile modulus		ISO 527-2/1	6100 Mpa
tensile strength	Break	ISO 527-2/5	82.0 Mpa
Tensile modulus		ASTM D638/ISO 527	6100 kg/cm²(MPa)[Lb/in²]
Elongation at Break		ASTM D638/ISO 527	1.0 %
tensile strength		ASTM D638/ISO 527	82.0 kg/cm²(MPa)[Lb/in²]
Physical properties	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
Water absorption rate	23°C,24hr	ISO 62	0.14 %
Shrinkage rate		ASTM D955	0.40-0.60 %
Shrinkage rate		TD:4.00mm	Internal Method	0.40-0.60 %
Water absorption rate		ASTM D570/ISO 62	0.14 %
Shrinkage rate	MD:4.00mm	Internal Method	0.10-0.30 %
flammability	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
UL flame retardant rating	0.40mm	UL 94	V-2
Hot filament ignition temperature	1.6mm	IEC 60695-2-13	850 °C
Hot filament ignition temperature		1.0mm	IEC 60695-2-13	825 °C
Burning wire flammability index	1.6mm	IEC 60695-2-12	960 °C
Hot filament ignition temperature	3.0mm	IEC 60695-2-13	850 °C
Burning wire flammability index	3.0mm	IEC 60695-2-12	960 °C
UL flame retardant rating	1.6mm	UL 94	V-0
UL flame retardant rating		1.0mm	UL 94	V-1
Burning wire flammability index	1.0mm	IEC 60695-2-12	960 °C
thermal performance	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
Linear coefficient of thermal expansion		ASTM D696/ISO 11359	0.000030 mm/mm.℃
RTI Imp	1.5mm	UL 746	80.0 °C
Vicat softening temperature		ASTM D1525/ISO R306	147 ℃（℉）
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	140 °C
Vicat softening temperature		ISO 306/B50	147 °C
Hot deformation temperature	HDT	ASTM D648/ISO 75	145 ℃（℉）
Linear coefficient of thermal expansion	MD	ISO 11359-2	3E-05 cm/cm/°C
RTI Str	1.5mm	UL 746	80.0 °C
Hot deformation temperature	0.45MPa,Unannealed	ISO 75-2/B	145 °C
Linear coefficient of thermal expansion	TD	ISO 11359-2	6E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	80.0 °C
Electrical performance	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
Dielectric constant	100Hz	IEC 60250	3.40
Dissipation factor	100Hz	IEC 60250	1E-03
Dielectric loss		ASTM D150/IEC 60250	0.0010
Volume resistivity		IEC 60093	>1.0E+15 ohms·cm
Dissipation factor	1MHz	IEC 60250	9E-03
Surface resistivity		IEC 60093	>1.0E+15 ohms
Dielectric strength		IEC 60243-1	35 KV/mm
Dielectric constant	1MHz	IEC 60250	3.40
Surface resistivity		ASTM D257/IEC 60093	1.0E+15 Ω
Compared to the anti leakage trace index		IEC 60112	PLC 3
Dielectric constant		ASTM D150/IEC 60250	3.40
Volume resistivity		ASTM D257/IEC 60093	1.0E+15 Ω.cm
other	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
remarks			以上加工数据.为参考值.以生产厂商设备的实际状况而进行调整。
impact performance	Test Condition	Test Method	TEIJIN JAPAN/GN-3620L
Impact strength of simply supported beam without notch		ISO 179	40 kJ/m²