PA6 2210G6 NAN YA TAIWAN
--
Fitness equipment、Electrical field、Electronic field
High rigidity
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Mechanical properties | Test Condition | Test Method | NAN YA TAIWAN/2210G6 |
|---|---|---|---|
| tensile strength | D638 | 1700 kg/cm2 | |
| Flexural modulus | ASTM D790/ISO 178 | 76000 kg/cm²(MPa)[Lb/in²] | |
| Shrinkage rate | 3mm | D1505 | 0.2-0.6 % |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 12 kg·cm/cm(J/M)ft·lb/in | |
| Impact strength of cantilever beam gap | 3.2mm | D256 | 12 kg.cm/cm |
| tensile strength | ASTM D638/ISO 527 | 1700 kg/cm²(MPa)[Lb/in²] | |
| Flexural modulus | D790 | 76000 kg/cm2 |
| Physical properties | Test Condition | Test Method | NAN YA TAIWAN/2210G6 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.2-0.6 % | |
| density | ASTM D792/ISO 1183 | 1.35 | |
| melt mass-flow rate | ASTM D1238/ISO 1133 | 10 g/10min | |
| Water absorption rate | ASTM D570/ISO 62 | 2.8 % |
| physical property | Test Condition | Test Method | NAN YA TAIWAN/2210G6 |
|---|---|---|---|
| melt mass-flow rate | D1238 | 10 g/10min | |
| Water absorption rate | 24h/23℃ | D570 | 2.8 % |
| Thermal performance | Test Condition | Test Method | NAN YA TAIWAN/2210G6 |
|---|---|---|---|
| Heat distortion temperature | 18.6kg/cm2，HDT | D648 | 205 °C |
| HDT | ASTM D648/ISO 75 | 205 ℃（℉） |