PC+ABS Infino NE-1030 LOTTE KOREA
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| Charpy Notched Impact Strength | 23°C | ISO 179/1eA | 17 kJ/m² |
| Impact strength of cantilever beam gap | 23°C,6.35mm | ASTM D256 | 120 J/m |
| 23°C | ISO 180/1A | 16 kJ/m² | |
| 23°C,3.18mm | ASTM D256 | 490 J/m |
| hardness | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 118 |
| Mechanical properties | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| elongation | 断裂 | ASTM D638 | 59 % |
| Flexural modulus | ASTM D790 | 2500 MPa | |
| Tensile modulus | ASTM D638 | 2600 MPa | |
| tensile strength | 断裂 | ASTM D638 | 54.0 MPa |
| Tensile modulus | ISO 527-2/50 | 2500 MPa | |
| tensile strength | 屈服 | ASTM D638 | 63.0 MPa |
| Flexural modulus | ISO 178 | 2500 MPa | |
| bending strength | ASTM D790 | 87.0 MPa | |
| Tensile strain | 断裂 | ISO 527-2/50 | 35 % |
| bending strength | ISO 178 | 90.0 MPa | |
| tensile strength | 屈服 | ISO 527-2/50 | 60.0 MPa |
| 断裂 | ISO 527-2/50 | 46.0 MPa |
| flammability | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| UL flame retardant rating | 3.0mm | UL 94 | V-0 |
| 1.5mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| Shrinkage rate | MD：3.20mm | ASTM D955 | 0.32to0.39 % |
| TD:3.20mm | ISO 2577 | 0.33to0.40 % | |
| TD：3.20mm | ASTM D955 | 0.33to0.40 % | |
| density | ASTM D792 | 1.18 g/cm³ | |
| ISO 1183 | 1.18 g/cm³ | ||
| melt mass-flow rate | 220°C/10.0kg | ASTM D1238 | 53 g/10min |
| 220°C/10.0kg | ISO 1133 | 53 g/10min | |
| Shrinkage rate | MD:3.20mm | ISO 2577 | 0.32to0.39 % |
| Thermal performance | Test Condition | Test Method | LOTTE KOREA/Infino NE-1030 |
|---|---|---|---|
| Heat distortion temperature | 1.8MPa,Unannealed,4.00mm，HDT | ISO 75-2/A | 77.0 °C |
| 1.8MPa,未退火,6.40mm，HDT | ASTM D648 | 83.0 °C | |
| vicat | -- | ISO 306/B120 | 95.0 °C |
| Heat distortion temperature | 0.45MPa,Unannealed,4.00mm，HDT | ISO 75-2/B | 90.0 °C |
| 1.8MPa,Annealed,4.00mm，HDT | ISO 75-2/A | 85.0 °C | |
| vicat | -- | ISO 306/B50 | 93.0 °C |
| Heat distortion temperature | 0.45MPa,Annealed,4.00mm，HDT | ISO 75-2/B | 93.0 °C |