Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

POM Z3010 ASAHI JAPAN

TENAC™

Electrical applications,Household daily necessities,Engineering accessories,Application in the automotive field,Shell,Engine parts

High impact resistance,Medium viscosity

Plastic Datasheets

hardness	Test Condition	Test Method	ASAHI JAPAN/Z3010
Rockwell hardness	M-Scale	ASTM D785	94
Rockwell hardness		R-Scale	ASTM D785	120

thermal performance	Test Condition	Test Method	ASAHI JAPAN/Z3010
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	133 °C
		0.45MPa,Unannealed	ISO 75-2/B	163 °C
		1.8MPa,Unannealed	ISO 75-2/A	100 °C
		0.45MPa,Unannealed	ASTM D648	172 °C
Linear coefficient of thermal expansion	MD	ASTMD696	1E-04 cm/cm/°C
specific heat			1470 J/kg/°C
thermal conductivity			0.23 W/m/K

mechanical properties	Test Condition	Test Method	ASAHI JAPAN/Z3010
Bending modulus	--	ISO 178	2800 Mpa
Bending modulus		--	ASTM D790	2700 Mpa
bending strength		ASTM D790	96.0 Mpa
elongation	Break	ASTMD638	50 %
Taber abraser		ASTM D1044	13.0 mg
Tensile modulus		ISO 527-2	3000 Mpa
tensile strength	--	ASTM D638	69.0 Mpa
tensile strength		Yield	ISO 527-2	70.0 Mpa

Electrical performance	Test Condition	Test Method	ASAHI JAPAN/Z3010
Arc resistance		ASTM D495	250 sec
Dielectric constant	23°C,1MHz	ASTM D150	3.80
Dielectric strength		ASTM D149	18 KV/mm
Dissipation factor	23°C,1MHz	ASTM D150	7E-03
Surface resistivity		ASTM D257	1.0E+16-1.0E+17 ohms
Volume resistivity	23°C	ASTM D257	1.0E+15-1.0E+16 ohms·cm

Physical properties	Test Condition	Test Method	ASAHI JAPAN/Z3010
melt mass-flow rate	190°C/2.16kg	ISO 1133	2.4 g/10min
Shrinkage rate	MD	Internal Method	1.8-2.2 %
Water absorption rate	23°C,24hr,50%RH	ASTM D570	0.20 %

flammability	Test Condition	Test Method	ASAHI JAPAN/Z3010
UL flame retardant rating		UL 94	HB