Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PA66 CM3001R TORAY JAPAN
Amilan®
OA device
Low warpage
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| Rockwell hardness | M计秤,23°C | 83 -- | |
| R计秤,23°C | 120 -- |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| elongation at break | 80℃ | D638 | 8.5 % |
| Impact strength of cantilever beam gap | ASTM D256/ISO 179 | 45 kg·cm/cm(J/M)ft·lb/in | |
| Flexural modulus | -40°C | MPa | 6200 -- |
| Impact strength of cantilever beam gap | 23℃ | D256 | 45 J/m |
| tensile strength | 屈服,23℃ | D638 | 95 Mpa |
| Flexural modulus | 23℃ | D790 | 6.0 GPa |
| ASTM D790/ISO 178 | 3500 kg·cm/cm(J/M)ft·lb/in | ||
| bending strength | ASTM D790/ISO 178 | 125 kg·cm/cm(J/M)ft·lb/in | |
| elongation at break | ASTM D638/ISO 527 | 12 % | |
| bending strength | 23℃ | D790 | 150 Mpa |
| Rockwell hardness | ASTM D785 | 120 | |
| tensile strength | 屈服,-40℃ | D638 | 120 Mpa |
| 23°C | MPa | 95.0 70.0 | |
| 屈服,80℃ | D638 | 40 Mpa | |
| Flexural modulus | 23°C | MPa | 5800 3000 |
| bending strength | -40℃ | D790 | 180 Mpa |
| Tensile strain | 断裂,-40°C | % | 3.0 -- |
| Flexural modulus | 80℃ | D790 | 2.1 GPa |
| bending strength | 23°C | 155 MPa | |
| Tensile strain | 断裂,23°C | % | 3.5 5.0 |
| tensile strength | -40°C | MPa | 120 -- |
| bending strength | 80°C | MPa | 65.0 -- |
| tensile strength | ASTM D638/ISO 527 | 85 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂,80°C | % | 5.0 -- |
| Flexural modulus | -40℃ | D790 | 6.4 GPa |
| bending strength | 80℃ | D790 | 60 Mpa |
| elongation at break | 23℃ | D638 | 6.0 % |
| Flexural modulus | 80°C | MPa | 2000 -- |
| elongation at break | -40℃ | D638 | 5.0 % |
| bending strength | -40°C | MPa | 185 -- |
| tensile strength | 80°C | MPa | 40.0 -- |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| Volume resistivity | ASTM D257/IEC 60093 | 10^13 Ω.cm |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| density | ASTM D792/ISO 1183 | 1.19 | |
| Water absorption rate | ASTM D570/ISO 62 | 1.1 % |
| processability | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| Shrinkage rate | 3mmt | 1.0-1.4 % |
| physical property | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| Water absorption rate | 23℃,水中 | D570 | 5.1 % |
| Shrinkage rate | MD:3.00mm3 | % | 0.70-1.0 -- |
| Water absorption rate | 饱和,23°C | % | 5.1 -- |
| filler content | 40 wt% | ||
| Shrinkage rate | TD:3.00mm2 | % | 1.0-1.4 -- |
| Water absorption rate | 23℃,24hrs | D570 | 0.6 % |
| 23°C,24hr | % | 0.60 -- |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/CM3001R |
|---|---|---|---|
| Combustibility (rate) | UL 94 | HB | |
| Heat distortion temperature | 0.45MPa,未退火，HDT | °C | 243 -- |
| 0.46Mpa，HDT | D648 | 243 °C | |
| HDT | ASTM D648/ISO 75 | 224 ℃（℉） | |
| melting temperature | °C | 265 -- | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | °C | 185 -- |
| melting temperature | DSC | 265 °C | |
| Heat distortion temperature | 1.86MPa，HDT | D648 | 185 °C |
| melting temperature | 265 ℃（℉） |