Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PC DF-1008 SABIC INNOVATIVE US
LNP™ THERMOCOMP™
Plastic bag,Electrical appliances
Easy to demould,Easy to form,Filler: Glass fiber reinf,40% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1008 |
|---|---|---|---|
| Suspended wall beam without notch impact strength | 23°C | ISO 180/1U | 45 kJ/m² |
| Impact strength of cantilever beam gap | 23°C | ASTM D256 | 150 J/m |
| 23°C | ASTM D4812 | 720 J/m | |
| 23°C | ISO 180/1A | 14 kJ/m² |
| thermal performance | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1008 |
|---|---|---|---|
| Heat Deflection Temperature | 1.8MPa,未退火,64.0mm跨距，HDT | ISO 75-2/Af | 140 °C |
| 0.45MPa,未退火,3.20mm，HDT | ASTM D648 | 138 °C | |
| 1.8MPa,未退火,3.20mm，HDT | ASTM D648 | 134 °C | |
| 0.45MPa,Unannealed,64.0mmSpan，HDT | ISO 75-2/Bf | 141 °C |
| mechanical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1008 |
|---|---|---|---|
| Tensile modulus | ISO 527-2/1 | 14400 Mpa | |
| Tensile strain | 断裂 | ISO 527-2/5 | 6.9 % |
| tensile strength | 断裂 | ISO 527-2/5 | 132 Mpa |
| Tensile modulus | ASTM D638 | 22400 Mpa | |
| bending strength | 断裂,50.0mm跨距 | ASTM D790 | 205 Mpa |
| elongation | 断裂 | ASTM D638 | 6.5 % |
| flexural modulus | 50.0mm跨距 | ASTM D790 | 11600 Mpa |
| tensile strength | 断裂 | ASTM D638 | 141 Mpa |
| flexural modulus | ISO 178 | 11200 Mpa |
| Physical properties | Test Condition | Test Method | SABIC INNOVATIVE US/DF-1008 |
|---|---|---|---|
| density | ISO 1183 | 1.12 g/cm³ | |
| Water absorption rate | 24hr,50%RH | ASTM D570 | 0.080 % |
| shrinkage rate | MD：24小时 | ASTM D955 | 1.0-3.0 % |
| TD：24hr | ASTM D955 | 0.30-0.50 % | |
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.080 % |
| density | ASTM D792 | 1.12 g/cm³ |