PA6 C3U PA6 vs. - Plastic Material Properties Comparison Chart at Plas.com

Material Selector

All

Plastic Materials Additives Masterbatch Material Selector Price Index Trade Data Plastic News About Us

Material Comparison

Add Comparison Model

Select Products for Comparison (1/4)

Highlight Differences

Hide Same

Product Name / Manufacturer / Model

Grade

Certificates

Reference Price

PA6 BASF GERMANY C3U

Injection grade

US$ 5,870 / MT

FOB Guangzhou port, China

thermal performance	Test Condition	Test Method	BASF GERMANY/C3U
RTI Elec	0.38mm	UL 746	110 °C
Melting temperature		ISO 3146	243 °C
RTI Imp	0.38mm	UL 746	65.0 °C
RTI Imp		3.0mm	UL 746	105 °C
Hot deformation temperature	0.45MPa,Unannealed	ASTM D648	224 °C
Melting temperature		ASTM D3418	243 °C
Linear coefficient of thermal expansion	TD		9E-05 cm/cm/°C
RTI Str	0.75mm	UL 746	115 °C
RTI Imp	1.5mm	UL 746	105 °C
RTI Elec	3.0mm	UL 746	120 °C
RTI Str	3.0mm	UL 746	120 °C
Hot deformation temperature	1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
Linear coefficient of thermal expansion	MD	ASTME831	4E-05 cm/cm/°C
RTI Imp	0.75mm	UL 746	105 °C
RTI Str	0.38mm	UL 746	65.0 °C
RTI Str		1.5mm	UL 746	120 °C
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	91.0 °C
Linear coefficient of thermal expansion	MD		8E-05 cm/cm/°C
RTI Elec	1.5mm	UL 746	120 °C
RTI Elec		0.75mm	UL 746	120 °C
Physical properties	Test Condition	Test Method	BASF GERMANY/C3U
density		ISO 1183	1.16 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	140 cm3/10min
Shrinkage rate	MD：3.18mm		0.80 %
density		ASTM D792	1.16 g/cm³
Water absorption rate	Equilibrium,50%RH	ASTM D570	2.9 %
		Equilibrium,23°C,50%RH	ISO 62	2.9 %
		Saturation,23°C	ISO 62	8.5 %
		Saturation	ASTM D570	8.5 %
hardness	Test Condition	Test Method	BASF GERMANY/C3U
Ball Pressure Test		ISO 2039-1	100 Mpa
impact performance	Test Condition	Test Method	BASF GERMANY/C3U
Impact strength of cantilever beam gap	-40°C	ASTM D256	32 J/m
Charpy Notched Impact Strength	-30°C	ISO 179	4.0 kJ/m²
Charpy Notched Impact Strength		23°C	ISO 179	9.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ASTM D256	43 J/m
Impact strength of cantilever beam gap		23°C	ISO 180	4.5 kJ/m²
Impact strength of simply supported beam without notch	23°C	ISO 179	80 kJ/m²
mechanical properties	Test Condition	Test Method	BASF GERMANY/C3U
tensile strength	Yield,23°C	ASTM D638	83.0 Mpa
Bending modulus	23°C	ASTM D790	3000 Mpa
elongation	Yield,23°C	ASTM D638	5.0 %
Tensile modulus	23°C	ISO 527-2	3500 Mpa
tensile strength	Yield,23°C	ISO 527-2	75.0 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
Bending modulus	23°C	ISO 178	3000 Mpa
elongation	Break,23°C	ASTM D638	50 %
Nominal tensile fracture strain	23°C	ISO 527-2	6.0 %
Electrical performance	Test Condition	Test Method	BASF GERMANY/C3U
Volume resistivity	1.50mm	ASTM D257	1E+13 ohms·cm
Volume resistivity			IEC 60093	1E+13 ohms·cm
Dissipation factor	1MHz	IEC 60250	0.020
Dielectric strength		IEC 60243-1	32 KV/mm
Dielectric constant	1MHz	IEC 60250	3.60
Compared to the anti leakage trace index		IEC 60112	PLC 0
flammability	Test Condition	Test Method	BASF GERMANY/C3U
UL flame retardant rating	1.5mm	UL 94	V-0
		0.75mm	UL 94	V-0
		3.0mm	UL 94	V-0
		0.38mm	UL 94	V-0