Material Comparison

Product Info

Product Name

Brand Name

Usages

Properties

Certificates

PA6 C3U BASF GERMANY

Ultramid®

Electrical components,Electronic insulation

High impact resistance,Flame retardant

Plastic Datasheets

hardness	Test Condition	Test Method	BASF GERMANY/C3U
Ball Pressure Test		ISO 2039-1	100 Mpa

thermal performance	Test Condition	Test Method	BASF GERMANY/C3U
Hot deformation temperature	1.8MPa,Unannealed	ASTM D648	91.0 °C
		1.8MPa,Unannealed	ISO 75-2/A	70.0 °C
		0.45MPa,Unannealed	ASTM D648	224 °C
Linear coefficient of thermal expansion	MD	ASTME831	4E-05 cm/cm/°C
		TD		9E-05 cm/cm/°C
		MD		8E-05 cm/cm/°C
Melting temperature		ASTM D3418	243 °C
Melting temperature			ISO 3146	243 °C
RTI Elec	0.38mm	UL 746	110 °C
		3.0mm	UL 746	120 °C
		0.75mm	UL 746	120 °C
		1.5mm	UL 746	120 °C
RTI Imp	0.38mm	UL 746	65.0 °C
		1.5mm	UL 746	105 °C
		3.0mm	UL 746	105 °C
		0.75mm	UL 746	105 °C
RTI Str	3.0mm	UL 746	120 °C
		0.38mm	UL 746	65.0 °C
		1.5mm	UL 746	120 °C
		0.75mm	UL 746	115 °C

mechanical properties	Test Condition	Test Method	BASF GERMANY/C3U
Bending modulus	23°C	ISO 178	3000 Mpa
Bending modulus		23°C	ASTM D790	3000 Mpa
elongation	Yield,23°C	ASTM D638	5.0 %
elongation		Break,23°C	ASTM D638	50 %
Nominal tensile fracture strain	23°C	ISO 527-2	6.0 %
Tensile modulus	23°C	ISO 527-2	3500 Mpa
Tensile strain	Yield,23°C	ISO 527-2	4.0 %
tensile strength	Yield,23°C	ASTM D638	83.0 Mpa
tensile strength		Yield,23°C	ISO 527-2	75.0 Mpa

Electrical performance	Test Condition	Test Method	BASF GERMANY/C3U
Compared to the anti leakage trace index		IEC 60112	PLC 0
Dielectric constant	1MHz	IEC 60250	3.60
Dielectric strength		IEC 60243-1	32 KV/mm
Dissipation factor	1MHz	IEC 60250	0.020
Volume resistivity		IEC 60093	1E+13 ohms·cm
Volume resistivity		1.50mm	ASTM D257	1E+13 ohms·cm

Physical properties	Test Condition	Test Method	BASF GERMANY/C3U
density		ISO 1183	1.16 g/cm³
density			ASTM D792	1.16 g/cm³
Melt Volume Flow Rate (MVR)	275°C/5.0kg	ISO 1133	140 cm3/10min
Shrinkage rate	MD：3.18mm		0.80 %
Water absorption rate	Saturation	ASTM D570	8.5 %
		Equilibrium,23°C,50%RH	ISO 62	2.9 %
		Equilibrium,50%RH	ASTM D570	2.9 %
		Saturation,23°C	ISO 62	8.5 %

impact performance	Test Condition	Test Method	BASF GERMANY/C3U
Charpy Notched Impact Strength	-30°C	ISO 179	4.0 kJ/m²
Charpy Notched Impact Strength		23°C	ISO 179	9.0 kJ/m²
Impact strength of cantilever beam gap	23°C	ISO 180	4.5 kJ/m²
		23°C	ASTM D256	43 J/m
		-40°C	ASTM D256	32 J/m
Impact strength of simply supported beam without notch	23°C	ISO 179	80 kJ/m²

flammability	Test Condition	Test Method	BASF GERMANY/C3U
UL flame retardant rating	0.75mm	UL 94	V-0
		3.0mm	UL 94	V-0
		0.38mm	UL 94	V-0
		1.5mm	UL 94	V-0