AES ESA20-450 UMG JAPAN
DIALAC®
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| hardness | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| Rockwell hardness | ISO 2039-2 | 110 R |
| Mechanical properties | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| bending strength | 23°C | ISO 178 | 80 Mpa |
| Charpy Notched Impact Strength | -30°C | ISO 179/1eA | 4.0 kJ/m² |
| 23°C | ISO 179/1eA | 11 kJ/m² | |
| Flexural modulus | 23°C | ISO 178 | 2700 Mpa |
| Tensile modulus | 23°C | ISO 527-2 | 2600 Mpa |
| tensile strength | 23°C | ISO 527-2 | 50 Mpa |
| Electrical performance | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| dielectric strength | IEC 60243-1 | 32 KV/mm | |
| Volume resistivity | IEC 60093 | 1E+15 Ω.cm |
| Flame retardant performance | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| UL flame retardant rating | UL -94 | HB 1.50mm | |
| UL -94 | HB 3.00mm |
| physical property | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| melt mass-flow rate | 220℃/10Kg | ISO 1133 | 22.00 cm3/10min |
| Shrinkage rate | MD2.0mm | ISO 294-4 | 0.65 % |
| Thermal performance | Test Condition | Test Method | UMG JAPAN/ESA20-450 |
|---|---|---|---|
| Heat distortion temperature | 1.80MPa退火，HDT | ISO 75-2/Af | 83 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 7E-05 cm/cm/°C |