PA/MXD6 1371 BLK01 MITSUBISHI ENGINEERING JAPAN
RENY™
Electronic and Electrical、Automotive sector
High rigidity、High impact、Filler: Glass fiber reinf、55% filler by weight
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Impact resistance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1371 BLK01 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 93 kJ/m² |
| Mechanical properties | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1371 BLK01 |
|---|---|---|---|
| Tensile modulus | ISO 527-2 | 20800 Mpa | |
| bending strength | ISO 178 | 403 Mpa | |
| Tensile strain | 断裂 | ISO 527-2 | 1.9 % |
| Flexural modulus | ISO 178 | 19600 Mpa | |
| tensile strength | 断裂 | ISO 527-2 | 242 Mpa |
| flammability | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1371 BLK01 |
|---|---|---|---|
| UL flame retardant rating | -- | UL 94 | HB |
| 1.6mm | UL 94 | HB |
| physical property | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1371 BLK01 |
|---|---|---|---|
| Shrinkage rate | 0.40 % | ||
| Water absorption rate | 平衡,23°C,50%RH | ISO 62 | 0.90 % |
| 饱和,23°C | ISO 62 | 0.11 % |
| Thermal performance | Test Condition | Test Method | MITSUBISHI ENGINEERING JAPAN/1371 BLK01 |
|---|---|---|---|
| Heat distortion temperature | 0.45MPa,未退火，HDT | ISO 75-2/B | 236 °C |
| 1.8MPa,未退火，HDT | ISO 75-2/A | 227 °C |