Material Comparison
Product Info
Product Name
Brand Name
Usages
Properties
Certificates
PPS A504X90 TORAY JAPAN
Torelina®
Automotive sector、Electrical components、sporting goods、small home appliances
Chemical resistance、Flame retardant、Glass fiber reinforced、High impact resistance、High temperature resistan
UL
--
--
--
--
--
--
--
--
--
--
--
--
--
--
--
Plastic Datasheets
| Other performance | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| 320℃,98MPa，流动长 | TORAY | 100 |
| Impact resistance | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Impact strength of simply supported beam without notch | 23°C | ISO 179 | 55 kJ/m² |
| hardness | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Rockwell hardness | R级 | ISO 2039-2 | 122 |
| Supplementary Information | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| BarFlowLength | 320°C,1.00mm | 内部方法 | 135 mm |
| Basic performance | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Water absorption rate | 24hr,23℃于水中 | ASTM D-570 | 0.02 % |
| Electrical performance | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| dielectric constant | 23°C,1MHz | IEC 60250 | 4.20 |
| dielectric strength | ASTM D-149 | 21 MV/m | |
| IEC 60243-1 | 24 KV/mm | ||
| Volume resistivity | IEC 60093 | 1E+16 ohms·cm | |
| dielectric constant | ASTM D150/IEC 60250 | 4.2 | |
| Dissipation Factor | 10 | ASTM D-150 | 0.002 |
| arc resistance | ASTM D-495 | 127 | |
| Volume resistivity | ASTM D257/IEC 60093 | 1014 Ω.cm | |
| dielectric constant | 10 | ASTM D-150 | 3.8 |
| Volume resistivity | ASTM D-257 | 10 Ω.m | |
| Dissipation Factor | 23°C,1MHz | IEC 60250 | 2E-03 |
| Mechanical properties | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| bending strength | ASTM D790/ISO 178 | 305 kg/cm²(MPa)[Lb/in²] | |
| shear strength | 23°C | JISK7214 | 80.0 Mpa |
| Flexural modulus | ASTM D790/ISO 178 | 15.5 kg/cm²(MPa)[Lb/in²] | |
| Impact strength of cantilever beam gap | 缺口 | ASTM D-256 | 130 J/m |
| Flexural modulus | 23℃ | ASTM D-790 | 13.3 GPa |
| coefficient of friction | 0.25 | ||
| elongation at break | ASTM D638/ISO 527 | 1.8 % | |
| Taber abraser | 1000Cycles | ISO 9352 | 50.0 mg |
| Rockwell hardness | ASTM D785 | 122 | |
| tensile strength | ASTM D638/ISO 527 | 200 kg/cm²(MPa)[Lb/in²] | |
| Tensile strain | 断裂,23°C | ISO 527-2 | 1.8 % |
| bending strength | 23°C | ISO 178 | 305 Mpa |
| elongation at break | 23℃ | ASTM D-638 | 3.6 % |
| Rockwell hardness | ASTM D-785 | 122 R | |
| compressive strength | ASTM D-732 | 80 | |
| bending strength | 23℃ | ASTM D-790 | 275 Mpa |
| tensile strength | 屈服,23°C | ISO 527-2 | 200 Mpa |
| Flexural modulus | 23°C | ISO 178 | 15500 Mpa |
| Charpy Notched Impact Strength | ASTM D256/ISO 179 | 55 kg·cm/cm(J/M)ft·lb/in | |
| tensile strength | 23℃ | ASTM D-638 | 207 Mpa |
| Impact strength of cantilever beam gap | 无缺口 | ASTM D-256 | 55 KJ/m |
| other | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| characteristic | 40%加纤.增强.标准 |
| Physical properties | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Shrinkage rate | ASTM D955 | 0.36 % | |
| density | ASTM D792/ISO 1183 | 1.66 | |
| Water absorption rate | ASTM D570/ISO 62 | 0.02 % |
| flammability | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| UL flame retardant rating | 0.28mm | UL 94 | V-0 |
| physical property | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Taber wear resistance | ASTM D-D1044 | 50 mg/1000次 | |
| Shrinkage rate | TD:3.00mm2 | 内部方法 | 0.80 % |
| MD:3.00mm4 | 内部方法 | 0.20 % | |
| Water absorption rate | 23°C,24hr | ISO 62 | 0.020 % |
| Shrinkage rate | 垂直方向 | TORAY | 0.70 % |
| 流动方向 | TORAY | 0.20 % | |
| limiting pv value | TORAY | 815 KJ/m | |
| coefficient of friction | 对铁 | ASTM D-1894 | 0.25 |
| Thermal performance | Test Condition | Test Method | TORAY JAPAN/A504X90 |
|---|---|---|---|
| Combustibility (rate) | UL 94 | V-0 | |
| melting temperature | ISO 11357-3 | 278 °C | |
| Heat distortion temperature | 1.82MPa，HDT | ASTM D-648 | >260 °C |
| HDT | ASTM D648/ISO 75 | >260 ℃（℉） | |
| Linear coefficient of thermal expansion | 垂直方向 | ASTM D-696 | 3.2 |
| 流动方向 | ASTM D-696 | 2.3 | |
| Heat distortion temperature | 1.8MPa,未退火，HDT | ISO 75-2/A | 260 °C |
| Linear coefficient of thermal expansion | MD | ISO 11359-2 | 2.3E-05 cm/cm/°C |
| melting temperature | DSC | 278 °C | |
| 278 ℃（℉） | |||
| Linear coefficient of thermal expansion | TD | ISO 11359-2 | 3.1E-05 cm/cm/°C |